The phase transformations of the alloy Ti-40 mas % Nb after tempering and severe plastic deformation are studied. The phase transformations of the alloy according to the type and conditions of external influences are analyzed using methods of XRD, SEM and optical metallography. It is determined that inverse phase transformation of the metastable α''-phase to equilibrium β-phase is carried out after severe plastic deformation. Complete phase transformation α'' → β is typical for the mode, which consists of three pressing operation with the change of the loading axis in cramped conditions, followed by a multi-pass rolling in grooved rolls.

The influence of the microarc oxidation parameters as electrical voltage and process duration on the surface morphology and topography, wettability and chemical composition of calcium phosphate coatings on the low elastic module Ti-40mas.%Nb (Ti-40Nb) alloy surface has been investigated. The linear growth of thickness and roughness and the linear decrease of the free surface energy with increasing process electrical voltage have been obtained. It was shown that calcium phosphate coatings have low contact angle with liquids and high free surface energy, as a consequence. It indicates a high hydrophilicity. X-ray diffraction analyses showed that the coatings after deposition have X-ray amorphous state that indicates high rate of coating dissolution. The coatings have maximum Ca/P ratio is 0.6. The optimal range of the oxidation voltage from 200 to 250 V and process duration from 5 to 10 min has been found. Such parameters allow to form the coating with the specific morphology, roughness and thickness and high hydrophylicity.

The influence of the voltage of micro-arc oxidation on the physicochemical properties of the calciumphosphate coatings has been investigated. The linear growth of the roughness and hyperbolic decrease of the surface energy with growth of the oxidation voltage have been revealed. It was shown that the calciumphosphate coatings have low contact angle and high surface energy and, as a consequence, are hydrophilic. The optimal voltage range of the oxidation has been found. It varies from 200 to 250 V. This range provides the coating formation with the following specified parameters: surface roughness of 2 – 3.5 µm; contact angles with water and glycerol of 18 - 25º and 35 - 45º, respectively, and free surface energy of 73 - 80 mN/m.

Results of research of mechanical properties of calciumphosphate coatings produced by the method radio frequency magnetron sputtering on bioinert alloys of titanium, zirconium and were presented. Calcium phosphate coatings show high value of adhesion strength to bioinert metal surface. Calcium phosphate coating on titanium-niobium alloy surface shows the highest value of adhesion strength. Mechanical properties of a composite material based on bioinert alloy and calcium phosphate coating are higher than properties of the components of composite material separately.