Indium phosphide solar cells have a higher resistance to electron irradiation than Si or GaAs cells of comparable junction depth. As a result, there is much interest in the use of this material for space applications. Cells of this material were made in bulk InP by a number of techniques, including ion implantation, direct diffusion in sealed ampoules, and by open tube diffusion. However, it is generally considered that the epitaxial approach will be superior to all of these techniques. The epitaxy of InP is considerably more difficult than that of gallium arsenide, for a number of reasons. Perhaps the most important is the fact that the native oxides of Indium are extremely difficult to remove, as compared to that of Gallium. In addition, thermal treatments for the desorption of these oxides often result in the formation of phosphorus vacancies and free indium on the surface. Thus, inadequate sample preparation before epitaxy, poor reactor cleaning procedures, or poor transition procedures between the growth of successive layers, all give rise to trap phenomena and to high interface recombination velocities. Moreover, the lifetime of the grown material is dominated by the occurrence of native defects, so that it is a strong function of growth parameters. These problems are of special interest to the fabrication of solar cells, where long life-time, combined with the absence of traps, is highly desirable. A study of this problem is described using a non-invasive diagnostic technique which was developed.

This talk outlines a simple process for the fabrication of n(+)-p solar cells in indium phosphide. Large area cells (greater than 0.25 sq cm) have been made by this process, with a photovoltaic conversion efficiency of 15.21 percent under AM0 conditions of illumination. An ideality factor of 1.1 and a saturation current density of 8 x 10 to the minus 15th power A/sq cm have been observed for these cells. The technique for cell fabrication involves the diffusion of sulfur into InP by an open tube process, and gives highly reproducible results from run to run. A vacuum-deposited layer of gallium sulphide (Ga2S3) was used as the source for sulfur diffusion, with a chemically vapor deposited SiO2 cap layer to prevent decomposition of the InP surface during heat treatment. Diffusions were carried out in a flowing nitrogen ambient at 585 to 708 C, and characterized by their surface carrier concentration and the diffusion constant. The diffusion profile for sulfur in InP is estimated to be of the complementary error function type. The activation energy of the diffusion was estimated to be 1.94 eV. The technique described here is ideally suited for the fabrication of shallow n(+)-p junctions in InP, and has been used for space-borne solar cells.

Indium phosphide solar cells whose p-n junctions were processed by the open tube capped diffusion and by the closed tube uncapped diffusion of sulfur into Czochralski-grown p-type substrates are compared. Differences found in radiation resistance were attributed to the effects of increased base dopant concentration. Both sets of cells showed superior radiation resistance to that of gallium arsenide cells, in agreement with previous results. No correlation was, however, found between the open-circuit voltage and the temperature dependence of the maximum power.

A comparison is made between indium phosphide solar cells whose p-n junctions were processed by open tube capped diffusion, and closed tube uncapped diffusion, of sulfur into Czochralski grown p-type substrates. Air mass zero, total area, efficiencies ranged from 10 to 14.2 percent, the latter value attributed to cells processed by capped diffusion. The radiation resistance of these latter cells was slightly better, under 1 MeV electron irradiation. However, rather than being process dependent, the difference in radiation resistance could be attributed to the effects of increased base dopant concentration. In agreement with previous results, both cells exhibited radiation resistance superior to that of gallium arsenide. The lowest temperature dependency of maximum power was exhibited by the cells prepared by open tube capped diffusion. Contrary to previous results, no correlation was found between open circuit voltage and the temperature dependency of Pmax. It was concluded that additional process optimization was necessary before concluding that one process was better than another.

A simple open tube diffusion technique for the fabrication of n+p junction solar cells is described. Large area (greater than 0.25 square cm) solar cells have been made by this process with a photovoltaic conversion efficiency of 15.2 percent under simulated AMO illumination. An ideality factor is 1.04 and a saturation current density of 9.6 times 10 to the minus 16th power A/square cm have been observed for these cells. These are the lowest (best) values reported to date for diffused structures in bulk InP.

The authors describe the photovoltaic characteristics of an n+p junction solar cell fabricated on bulk InP by an open-tube-diffusion technique. Analysis of the forward characteristics shows that the forward current is dominated by recombination in the quasineutral regions, indicating that the fabrication technique produces a clean junction. Spectral response measurements are analyzed and more realistic boundary conditions are used to model the solar cell to determine important material and device parameters.

The feasibility of using bulk GaAs for the fabrication of diffused junction solar cells was determined. The effects of thermal processing of GaAs was studied, and the quality of starting bulk GaAs for this purpose was assessed. These cells are to be made by open tube diffusion techniques, and are to be tested for photovoltaic response under AMO conditions.

This paper describes the fabrication of solar cells made by a simple open tube p(+)-diffusion into bulk n-GaAs. In addition, cell performance is provided as an indicator of the quality of bulk GaAs for this application. Initial results using this technique (12.2 percent efficiency at AM1 for 0.5 sq cm cells) are promising, and indicate directions for materials improvement. It is shown that the introduction of the diffusant (zinc) with point defects significantly affects the material properties and results in an increase in current capability.

The photovoltaic characteristics of p(+)-n junction solar cells fabricated on bulk GaAs by an open tube diffusion technique are presented in detail. Quantum efficiency measurements were analyzed and compared to computer simulations of the cell structure in order to determine material parameters such as diffusion length, surface recombination velocity and junction depth. From the results obtained it is projected that proper optimization of the cell parameters can increase the efficiency of the cells to close to 20 percent.

The photovoltaic characteristics of P(+)N junction solar cells fabricated on bulk GaAs by an open tube diffusion technique are described in this paper.Spectral response measurements were analyzed in detail and compared to a computer simulation in order to determine important material parameters. It is projected that proper optimization of the cell parameters can increase the efficiency of the cells from 12.2 percent to close to 20 percent.

Recently melt grown GaAs, made by liquid encapsulation techniques, has become available. This material is of sufficiently good quality to allow the fabrication of solar cells by direct diffusion. Results obtained with p(+)/n junction solar cells made by zinc diffusion are described. The quality of bulk GaAs for this application is evaluated.