Owing to their insufficient light absorption and charge transport, 2D Ruddlesden-Popper (RP) perovskites show relatively low efficiency. In this work, methylammonium (MA), formamidinum (FA), and FA/MA mixed 2D perovskite solar cells (PSCs) are fabricated. Incorporating FA cations extends the absorption range and enhances the light absorption. Optical spectroscopy shows that FA cations substantially increase the portion of 3D-like phase to 2D phases, and X-ray diffraction (XRD) studies reveal that FA-based 2D perovskite possesses an oblique crystal orientation. Nevertheless, the ultrafast interphase charge transfer results in an extremely long carrier-diffusion length (≈1.98 µm). Also, chloride additives effectively suppress the yellow δ-phase formation of pure FA-based 2D PSCs. As a result, both FA/MA mixed and pure FA-based 2D PSCs exhibit a greatly enhanced power conversion efficiency (PCE) over 20%. Specifically, the pure FA-based 2D PSCs achieve a record PCE of 21.07% (certified at 20%), which is the highest efficiency for low-dimensional PSCs (n ≤ 10) reported to date. Importantly, the FA-based 2D PSCs retain 97% of their initial efficiency at 85 °C persistent heating after 1500 h. The results unambiguously demonstrate that pure-FA-based 2D PSCs are promising for achieving comparable efficiency to 3D perovskites, along with a better device stability.

Low-dimensional Ruddlesden-Popper perovskites (RPPs) exhibit excellent stability in comparison with 3D perovskites; however, the relatively low power conversion efficiency (PCE) limits their future application. In this work, a new fluorine-substituted phenylethlammonium (PEA) cation is developed as a spacer to fabricate quasi-2D (4FPEA)2 (MA)4 Pb5 I16 (n = 5) perovskite solar cells. The champion device exhibits a remarkable PCE of 17.3% with a Jsc of 19.00 mA cm-2 , a Voc of 1.16 V, and a fill factor (FF) of 79%, which are among the best results for low-dimensional RPP solar cells (n ≤ 5). The enhanced device performance can be attributed as follows: first, the strong dipole field induced by the 4-fluoro-phenethylammonium (4FPEA) organic spacer facilitates charge dissociation. Second, fluorinated RPP crystals preferentially grow along the vertical direction, and form a phase distribution with the increasing n number from bottom to the top surface, resulting in efficient charge transport. Third, 4FPEA-based RPP films exhibit higher film crystallinity, enlarged grain size, and reduced trap-state density. Lastly, the unsealed fluorinated RPP devices demonstrate superior humidity and thermal stability. Therefore, the fluorination of the long-chain organic cations provides a feasible approach for simultaneously improving the efficiency and stability of low-dimensional RPP solar cells.