Search

Kramers–Kronig transforms (KKT) constitute a powerful tool to validate experimental impedance data. A new algorithm, containing a Fast Fourier Transform (FFT) sub-routine, for the numerical calculus of the KKT has been developed. This algorithm is based in the convolution theorem and it uses only two FFT calculi. It was finally tested in the validation of an experimental transfer function for hydrogen permeation into an iron membrane. Unlike common algorithms for numerical integration, this algorithm allows the calculation of all frequencies at the same time at a high speed using a regular frequency interval for the whole calculation with the same or even higher precision. The FFT sub-routine is accessible in all languages so that the use of this code is very simple.

In this work, we present a pressure modulation method developed to study surface effects in hydrogen permeation through iron base alloys. The technique involves the generation of a sinusoidal hydrogen pressure on the input side of a permeation membrane and the measurement of the corresponding sinusoidal hydrogen flow, as an electrochemical current, at the exit side of the membrane. The obtained transfer function depends on both the bulk properties of the permeation membrane and the surface effects at the input and exit sides. By choosing appropriate membrane thickness and material, surface effects are rate determining and can be characterised. Studies of the effect of different Pd films electrodeposited on the input side of the permeation membrane show that there is a finite resistance for the transfer of hydrogen across the hydrogen/palladium interface.

A new transfer function for electrochemical hydrogen permeation through metallic membranes is defined, and its analytical expression is obtained through a theoretical model including surface processes and bulk diffusion. By means of the EIS technique combined with electrochemical hydrogen permeation, this transfer function was experimentally measured for iron membranes, covered with a thin layer of electrodeposited Pd at the exit side, immersed both in acid and alkaline media at the input cell. By fitting of the model to the experimental results a hydrogen diffusion coefficient in iron of 9.6 (±0.6) 10 −9 m 2 s −1 was obtained independently of both the membrane thickness and the input side solution pH in agreement with the values obtained by other authors with different techniques. It has been demonstrated that the oxide film formed on iron at the output side of the membrane delays hydrogen transport and that the thin Pd layer avoids the formation of this film without introducing new significant delays. The determination of the permeation transfer function allows to obtain relevant information about the electrochemical mechanisms of hydrogen discharge on the metallic surface.

Alloy 22 (UNS N06022) is a candidate material for the external wall of the high level nuclear waste containers for the potential repository site at Yucca Mountain. In the mill-annealed (MA) condition, Alloy 22 is a single face centered cubic phase. When exposed to temperatures on the order of 600 C and above for times higher than 1 h, this alloy may develop secondary phases that are brittle and offer a lower corrosion resistance than the MA condition. The objective of this work was to age Alloy 22 at temperatures between 482 C and 800 C for times between 0.25 h and 3,000 h and to study the corrosion performance of the resulting material. Aging was carried out using wrought specimens as well as gas tungsten arc welded (GTAW) specimens. The corrosion performance was characterized using standard immersion tests in aggressive acidic solutions and electrochemical tests in multi-component solutions. Results show that, in general, in aggressive acidic solutions the corrosion rate increased as the aging temperature and aging time increased. However, in multi ionic environments that could be relevant to the potential Yucca Mountain site, the corrosion rate of aged material was the same as the corrosion rate of the MA material.

The repassivation kinetics of AISI 304 austenitic stainless steel was studied in 0.5 M Na2SO4 solution, 1 M HCl solution and 1 M NaCl solution, at room temperature and at various electrode potentials. Under the experimental conditions used in the present work, stress corrosion cracking (SCC) of the steel was known to occur only in the HCl solutions. The repassivation kinetic results were described by relations of the type i = A·tb. In Na2SO4 solutions b = −1 was found. In NaCl solutions and in HCl solutions b = −1 was found only in the first 100 ms after straining. In the next 10 s a value of b = −0.5 was recorded, and for longer exposures values of b = 0.5 and b = 1 were observed. There is strong evidence that a dissolution-precipitation film formation mechanism is involved in the region where b = −0.5. By comparing the results in HCl solutions with those in NaCl solutions, slow repassivation, of the type b = −0.5, is concluded to be a necessary but not sufficient electrochemical condition for SCC susceptibility.