The behavior of solute atoms in an undersaturated Fe-3.3 at.%Ni model alloy upon heavy and light particle irradiations was investigated by Atom Probe Tomography. Whereas first irradiations, performed using 27 MeV Fe ions at 400 °C, highlight significant Ni enrichment on point defect clusters, solute-rich features detected after 2.8 MeV H + ion (400 °C) and 1 MeV electron (320 °C) irradiations are only associated with pre-existent microstructural defects. Nanoindentation tests show no hardening in light particle irradiated samples, strongly suggesting that no dislocation loop formed. These observations put forward the importance of point defect clusters resulting from displacement cascades in Ni clusters' formation. Image, graphical abstract [ABSTRACT FROM AUTHOR]

In situ irradiation in transmission electron microscope following pre-irradiation was performed on Fe-0.6Ni alloy to investigate the growth of dislocation loops under irradiation. The observations showed two types of loop growth behaviour. One type was almost linear growth with irradiation dose, possibly caused by loop absorbing freely migrating defects. The other was abrupt growth with rapid increase in diameter. It was found that nanometre-sized loop might migrate one-dimensionally, following which the large loop could absorb the small loop. This process can result in the abrupt growth of loop and broadening of loop size distribution. Image, graphical abstract [ABSTRACT FROM AUTHOR]

The microstructure and nanomechanical properties of three samples of the modified stainless steel (referred as the alloy D9) were systematically characterized after neutron irradiation in the Advanced Test Reactor. The samples were irradiated to 5.0, 8.2, and 9.2 displacements per atom at 448, 430, and 683°C, respectively. The evolutions of dislocation loops, cavities, and radiation-induced precipitates were quantitatively studied to reveal their dose and temperature dependencies. Nanohardness and nanoindentation creep tests were conducted at room temperature on the irradiated samples. Unexpected radiation hardening was observed in the highest-temperature-irradiated sample due to the formation of an unknown type of Ni- and Si-rich precipitates whose contributions to the radiation and mechanical performances of the alloy were discussed. We provide the radiation-microstructure-property correlations of alloy D9 with new insights, which can benefit the development and optimization of advanced austenitic alloys for future nuclear applications. Image, graphical abstract [ABSTRACT FROM AUTHOR]