Search

The paper deals with the dilatometric study of high-alloy martensitic tool steel with the designation M398 (BÖHLER), which is produced by the powder metallurgy process. These materials are used to produce screws for injection molding machines in the plastic industry. Increasing the life cycle of these screws leads to significant economic savings. This contribution focuses on creating the CCT diagram of the investigated powder steel in the range of cooling rates from 100 to 0.01 °C/s. JMatPro® API v7.0 simulation software was used to compare the experimentally measured CCT diagram. The measured dilatation curves were confronted with a microstructural analysis, which was evaluated using a scanning electron microscope (SEM). The M398 material contains a large number of carbide particles that occur in the form of M7C3 and MC and are based on Cr and V. EDS analysis was used to evaluate the distribution of selected chemical elements. A comparison of the surface hardness of all samples in relation to the given cooling rates was also carried out. Subsequently, the nanoindentation properties of the formed individual phases as well as the carbides, where the nanohardness and reduced modulus of elasticity (carbides and matrix) were evaluated. [ABSTRACT FROM AUTHOR]

The present work deals with the dilatometric study of a hot-rolled 0.2C3Mn1.5Si lean medium Mn steel, mainly suitable for the quenching and partitioning (Q&P) heat treatment in both hot-rolled or cold-rolled condition, subjected to a variation of austenitization temperature. These investigations were performed in a temperature range of 800–1200 °C. In this context, the martensite transformation start temperature (Ms) was determined as a function of austenitization temperature and in turn obtained prior austenite grain size (PAGS). The results show rise in prior austenite grain size due to increasing austenitization temperature, resulting in elevated Ms temperatures. Measured dilatation curves were confronted with the metallographic analysis by means of scanning electron microscopy (SEM). The present paper also focuses on the construction of a continuous cooling transformation (CCT) and deformation continuous cooling transformation (DCCT) diagram of the investigated lean medium Mn steel in a range of cooling rates from 100 to 0.01 °C/s and their subsequent comparison. By comparing these two diagrams, we observed an overall shift of the DCCT diagram to shorter times compared to the CCT diagram, which represents an earlier formation of phase transformations with respect to the individual cooling rates. Moreover, the determination of individual phase fractions in the CCT and DCCT mode revealed that the growth stage of ferrite and bainite is decelerated by deformation, especially for intermediate cooling rates. Microstructural changes corresponding to cooling were also observed using SEM to provide more detailed investigation of the structure and present phases identification as a function of cooling rate. Moreover, the volume fractions obtained from the saturation magnetization method (SMM) are compared with data from X-ray diffraction (XRD) measurements. The discussion of the data suggests that magnetization measurements lead to more reliable results and a more sensitive detection of the retained austenite than XRD measurements. In that regard, the volume fraction of retained austenite increased with a decrease of cooling rate as a result of larger volume fraction of ferrite and bainite. The hardness of the samples subjected to the deformation was slightly higher compared to non-deformed samples. The reason for this was an evident grain refinement after deformation. [ABSTRACT FROM AUTHOR]

The paper is focused on investigation of the high-strength AISI 4340 steel at various temperature and deformation conditions. The article is divided into two specific analyses. The first is to examine the dilatation behavior of the steel at eight different cooling rates, namely, 100, 10, 5, 1, 0.5, 0.1, 0.05 and 0.01 °C·s−1. The mapping of the phase transformations due to varying cooling rates from the austenitizing temperature of 850 °C allows the construction of the CCT diagram for a given high-strength steel. These dilatation curves were also compared with the metallography of the selected samples for the proper construction of the CCT diagram. A further analysis of the high temperature deformation of high strength steel AISI 4340 was performed in the range of temperature 900–1200 °C, and the strain rate was in the range from 0.001 to 10 s−1 with maximum value of the true strain 0.9. Changes in the microstructure were observed using light optical microscopy (LOM). The effect of hot deformation temperature on true stress, peak stress and true strain was investigated. The hardness of all deformed samples, depending on the temperature, the deformation rate and the peak stress σp overall together related with hardness, has also been evaluated. [ABSTRACT FROM AUTHOR]