Oxygen evolution reaction (OER) is critical in water splitting for green hydrogen gas production due to its sluggish kinetics; however, commercial OER catalysts commonly suffer from high cost, low catalytic activity and poor stability. Herein, we developed a C+ ion implantation method to modify single crystal diamond, and the resultant surface amorphous layer not only raised the active site number but also increased the content of the C=O group, thus significantly improving the OER activity. The C+ ion implanted high-temperature and high-pressure (C+-HTHP) and chemical vapor deposition (C+-CVD) diamonds both exhibit low OER overpotential with η 10 of 317 mV and 325 mV respectively, superior to those of HTHP diamond (360 mV), CVD diamond (395 mV) and RuO 2 (364 mV). The potentiostatic testing shows that the C+ implanted diamonds almost didn't undergo the rise of OER overpotential upon catalysis for more than 12 h at a current density of 10 mA cm−2, suggesting a high catalytic stability, owing to the strong bonding between single crystal diamond and amorphous carbon layer. For the first time, we utilized carbon ion implantation to prepare diamond-based high-performance OER catalyst, which broadens the understanding of carbon-based materials in OER catalysis. [ABSTRACT FROM AUTHOR]

The surface conductivity on the H-terminated diamond is still an interesting topic in the field of diamond electronics. Until now, the carrier mobility in the conductive channel has been limited to below 200cm2/Vs due to the various surface scattering mechanisms. In this paper, a high mobility conductive channel on the H-terminated diamond surface was reported. Firstly, the high quality diamond films were deposited on the commercial CVD diamond substrates. After polishing, the H-termination was obtained by hydrogen plasma treatment. The surface morphology of the H-terminated diamond was observed by atomic force microscope (AFM) and scanning electron microscope (SEM). The crystal quality on the diamond surface was characterized by Raman spectroscopy. The impurities in the crystals were tested by photoluminescence spectroscopy. The surface conductivity of H-terminated diamond was monitored comprehensively by Hall test. It can be found that the sheet resistance decreases much and the carrier mobility increases dramatically after the hydrogen plasma treatment and mechanical cleaning. The maximum mobility value is up to 365cm2/Vs with carrier density of 2.9 × 1012 cm−2, which is the highest value reported. Raman spectra of diamond surface show that a peak appears at 1121.4 cm−2 after the hydrogen plasma treatment, which corresponds to the nanocrystal diamond or carbon clusters of sp3 bonded material. The corresponding mobility enhancement mechanism on the H-terminated diamond surface was proposed. Unlabelled Image • The carrier mobility enhancement on the H-terminated diamond surface was found. • A thin carbon film on the diamond surface was observed with Raman peak at 1121 cm−1. • The H-terminated diamond surface showed high carrier mobility of 365cm2/Vs. • The corresponding mobility enhancement mechanism was proposed. [ABSTRACT FROM AUTHOR]