Search

The purpose of this study was to measure enamel wear caused by antagonistic monolithic zirconia crowns and to compare this with enamel wear caused by contralateral natural antagonists. Twenty monolithic zirconia full molar crowns were placed in 20 patients. Patients with high activity of the masseter muscle at night (bruxism) were excluded. For analysis of wear, vinylpolysiloxane impressions were prepared after crown incorporation and at 6-, 12-, and 24-month follow-up. Wear of the occlusal contact areas of the crowns, of their natural antagonists, and of two contralateral natural antagonists (control teeth) was measured by use of plaster replicas and a 3D laser-scanning device. Differences of wear between the zirconia crown antagonists and the control teeth were investigated by means of two-sided paired Student's t-tests and linear regression analysis. After 2 years, mean vertical loss was 46 μm for enamel opposed to zirconia, 19-26 μm for contralateral control teeth and 14 μm for zirconia crowns. Maximum vertical loss was 151 μm for enamel opposed to zirconia, 75-115 μm for control teeth and 60 μm for zirconia crowns. Statistical analysis revealed significant differences between wear of enamel by zirconia-opposed teeth and by control teeth. Gender, which significantly affected wear, was identified as a possible confounder. Monolithic zirconia crowns generated more wear of opposed enamel than did natural teeth. Because of the greater wear caused by other dental ceramics, the use of monolithic zirconia crowns may be justified. [ABSTRACT FROM AUTHOR]

To evaluate the in vitro fracture load of extensively damaged vital teeth after either direct or indirect restauration, severe tooth substance loss was simulated for 96 molars. Subsequently, two cavities were prepared with little (design 1) or more substantial (design 2) residual tooth support. All molars were provided with a 2-mm ferrule design and then divided into 12 test groups based on their occlusal surface size. They were restored with composite or with either of two types of single crown (cast metal or milled zirconia). After thermal ageing (10 000 cycles at 6·5 and 60 °C), 1·2 million cycles of chewing simulation were applied (64 N). Maximum fracture load was determined with a loading angle of 45°. Statistical analysis was performed by use of Kaplan-Meier modelling, Student's t-tests, one-way anova, post hoc Tukey's HSD tests and linear regression analysis. Regarding mean fracture load without ageing, the indirect restorations outperformed composite (design 1: direct: 508 ± 123 N, indirect: 741 ± 248 N; design 2: direct: 554 ± 167 N, indirect: 903 ± 221 N). After artificial ageing, however, these differences were no longer significant (design 1: direct: 328 ± 189 N, indirect: 506 ± 352 N; design 2: direct 399 ± 208 N, indirect 577 ± 292 N). Instead, the fracture load of the aged composite restorations was comparable with that for zirconia (design 1) and cast metal (design 2) crowns. Fracture loads of direct composite restorations after artificial ageing might fulfil clinical requirements. [ABSTRACT FROM AUTHOR]

The purpose of this study was to evaluate enamel wear caused by monolithic zirconia crowns and to compare this with enamel wear caused by contralateral natural antagonists. Twenty monolithic zirconia crowns were placed in 20 patients requiring full molar crowns. For measurement of wear, impressions of both jaws were made at baseline after crown cementation and at 6-month follow-up. Mean and maximum wear of the occlusal contact areas of the crowns, of their natural antagonists and of the two contralateral natural antagonists were measured by the use of plaster replicas and 3 D laser scanning methods. Wear differences were investigated by the use of two-sided paired Student's t-tests and by linear regression analysis. Mean vertical loss (maximum vertical loss in parentheses) was 10 (43) μm for the zirconia crowns, 33 (112) μm for the opposing enamel, 10 (58) μm for the contralateral teeth and 10 (46) μm for the contralateral antagonists. Both mean and maximum enamel wear were significantly different between the antagonists of the zirconia crowns and the contralateral antagonists. Gender and activity of the masseter muscle at night (bruxism) were identified as possible confounders which significantly affected wear. Under clinical conditions, monolithic zirconia crowns seem to be associated with more wear of opposed enamel than are natural teeth. With regard to wear behaviour, clinical application of monolithic zirconia crowns is justifiable because the amount of antagonistic enamel wear after 6 months is comparable with, or even lower than, that caused by other ceramic materials in previous studies. [ABSTRACT FROM AUTHOR]

The purpose of this in vitro study was to assess the breaking load of zirconia-based crowns veneered with either CAD/ CAM-produced or manually layered feldspathic ceramic. Thirty-two identical zirconia frameworks ( Sirona in Coris ZI, mono L F1), 0·6 mm thick with an anatomically shaped occlusal area, were constructed ( Sirona in Lab 3.80). Sixteen of the crowns were then veneered by the use of CAD/ CAM-fabricated feldspathic ceramic ( CEREC Bloc, Sirona) and 16 by the use of hand-layered ceramic. The CAD/ CAM-manufactured veneer was attached to the frameworks by the use of Panavia 2.0 ( Kuraray). Half of the specimens were loaded until failure without artificial ageing; the other half of the specimens underwent thermal cycling and cyclic loading (1·2 million chewing cycles, force magnitude Fmax = 108 N) before the assessment of the ultimate load. To investigate the new technique further, finite element ( FE) computations were conducted on the basis of the original geometry. Statistical assessment was made by the use of non-parametric tests. Initial breaking load was significantly higher in the hand-layered group than in the CAD/ CAM group (mean: 1165·86 N versus 395·45 N). During chewing simulation, however, 87·5% (7/8) of the crowns in the hand-layered group failed, whereas no crown in the CAD/ CAM group failed. The CAD/ CAM-produced veneer was significantly less sensitive to ageing than the hand-layered veneer. [ABSTRACT FROM AUTHOR]

The purpose of this prospective cohort study was to assess the performance of tooth-supported, long-span, zirconia fixed dental prostheses (FDPs). Thirty FDPs with span lengths from 36 to 46 mm (mean 40·33 mm), with 4-7 units and with connector dimensions ∼9 mm2 were inserted (19 in the posterior region, 11 including anterior teeth) using glass-ionomer cement. The performance of the FDPs was assessed (aesthetic evaluation, failures, hypersensitivity/tooth vitality, secondary caries, pocket depth, decementation, and chipping) at baseline and after 5 years. Cox regression analysis was performed to identify risk factors. There were 16 failures after 5 years. Framework fracture occurred for two FDPs, four FDPs had to be re-cemented, one abutment tooth had to be treated endodontically, one abutment tooth fractured and cohesive failure of the veneer occurred for eight. Four FDPs had to be replaced, so survival was 82%. The aesthetics were rated as excellent by the patients at baseline and good at the 5-year recall. Cox regression analysis showed that both length [ P = 0·05, exp(B) = 1·22] and location [ P = 0·019, exp(B) = 4·09] of the FDP were risk factors for failure. Compared with the previously published 2-year results, the incidence of complications increased dramatically. Additionally, it was shown that long-span FDPs in the molar region are at greater risk of failure than FDPs in the anterior region. [ABSTRACT FROM AUTHOR]

Aim of this study was to introduce a feasible and valid technique for the assessment of masticatory performance that is comparable to the standard sieving method. Twenty-one chewing samples (Optosil) comminuted by healthy dentate adults were analysed with a sieving and scanning method. Scanning was performed using a conventional flatbed scanner (1200 dpi). All scanned images underwent image analysis (ImageJ), which yielded descriptive parameters such as area, best-fitting ellipse for each particle. Of the 2D-image, a volume was estimated for each particle, which was converted into a weight. To receive a discrete distribution of particle sizes comparable to sieving, five chewing samples were used to calculate a size-dependent area-volume-conversion factor. The sieving procedure was carried out with a stack of 10 sieves, and the retained particles per sieve were weighed. The cumulated weights yielded by either method were curve-fitted with the Rosin-Rammler distribution to determine the median particle size x50. The Rosin-Rammler distributions for sieving and scanning resemble each other. The distributions show a high correlation (0·919-1·0, n = 21, P < 0·01, Pearson's correlation coefficient). The median particle sizes vary between 3·83 and 4·77 mm (mean: 4·31) for scanning and 3·53 and 4·55 mm (mean: 4·21) for sieving. On average, scanning overestimates the x50 values by 2·4%. A modified Bland-Altman plot reveals that 95% of the x50 values fall within 10% of the average x50. The scanning method is a valid, simple and feasible method to determine masticatory performance. [ABSTRACT FROM AUTHOR]