Search

Background/purpose: 4-methacryloyloxyethyl trimellitate anhydride/methyl methacrylate-tri-n-butyl borane (4-META/MMA-TBB) resin is used for indirect restorations. We aimed to evaluate effects of immersion in 4-META/MMA-TBB-activated liquid on the bond strength of root canal dentin. Materials and methods: We used freshly extracted single-rooted human teeth. After decoronation, each root was vertically sectioned into halves; their dentin walls were polished and flattened. The control group underwent dentin treatment with Green Activator. The immersion group was treated with Green Activator and Teeth Primer and immersed in 4-META/MMA-TBB-activated liquid. After bonding the resin blocks with Super-Bond, microtensile bond strength (μTBS) tests were performed (n = 6), and fracture surfaces were analyzed. Before surface treatment, dentin was immersed in a sodium fluorescein solution for 3 h, and resin blocks were bonded with Super-Bond with rhodamine B as in the bond strength test. The bonded cross section was observed using confocal laser scanning microscopy (CLSM). Results: μTBS was significantly higher in the immersion group than in the control group (61.5 [51.3–66.7] vs. 33.0 [20.4–57.8] MPa; P

Background/purpose: Recently, an effective core build-up system for teeth with flared root canals is needed. This research aimed to evaluate the effect of foundation restorations using a composite resin core with a fiber post reinforced with a zirconia tube for the surface strain at the cervical area and the fracture load of teeth with flared root canals. Materials and methods: Bovine teeth were shaped to mimic human premolars with flared root canals and restored using three types of composite resin foundation restorations with each materials described below: a fiber post (FC), a zirconia tube (ZC), a fiber post and zirconia tube (ZFC). Each specimen was restored with a zirconia crown. The surface strains of the specimens at the cervical area and fracture loads were analyzed using a one-way analysis of variance (ANOVA), followed by Tukey's honest significant difference test. Results: The surface strains of Groups ZFC and ZC were significantly lower than that of Group FC in the buccal root. The fracture strengths of Groups ZFC and ZC were significantly higher than that of Group FC. The strength of Group ZFC was significantly higher than that of Group ZC. Conclusion: The use of a composite resin core with a zirconia tube for the simulated premolar with flared root canals reduced surface strain at the cervical area and provided higher fracture strength compared to using a composite resin core with a fiber post. And the zirconia tubes provided even higher fracture strength when used with a fiber post.

Background/purpose: Retainer debonding of resin-bonded fixed dental prostheses (RBFDPs) is one of the major reasons for their lower survival rates than fixed dental prostheses (FDPs) with full-coverage crowns. Recent advances in milling technology have enabled the fabrication of RBFDPs with complex retainers (D-shaped designs). This study aimed to assess the marginal fit and retention force of zirconia RBFDPs with inlay-, L-, and D-shaped designs to clarify their clinical applications. Materials and methods: Three abutment teeth models without maxillary second premolars were created using inlay-, L-, and D-shaped retainer designs. The zirconia RBFDPs were designed and fabricated according to the manufacturer’s instructions (n = 10). The marginal gap was measured using the silicone replica technique. Zirconia frameworks were bonded to the abutment teeth using resin cement. Tensile test was conducted after thermal cycling and dynamic loading tests. The loads during debonding or fracture were recorded. The failure pattern was analyzed by observing the fracture surface using a scanning electron microscope. Results: D-shaped RBFDPs showed a significantly larger marginal gap than inlay- and L-shaped RBFDPs (P

Background/purpose: With the advancement of an over aging society, the average number of remaining teeth has increased. However, these remaining teeth do not always have sufficient alveolar bone support, and sometimes fabricated connected crowns are applied. This study evaluated the influence of crown material, crown thickness, and alveolar bone resorption on the stress distribution within the abutment teeth of connected crowns. Materials and methods: Using structural analysis software, a premolar crown model was fabricated. Three kinds of crown materials, two types of crown thickness, two types of post and core systems, and two levels of alveolar bone were assumed and evaluated for the stress distribution within the abutment teeth. Results: The higher material properties crown was, the more stress was concentrated at the marginal area. The composite resin core showed larger stress values around the marginal area, and the metal core showed larger stress values at the tip of the post. Alveolar bone resorption progressed, the marginal area stress value increased. Conclusion: The low elastic modulus crown material polyetheretherketone (PEEK) prevented stress concentrations at the marginal area of the crown and dentine, even with alveolar bone resorption. However, the amount of bone resorption has a great influence on the stress distribution around the tip of the post compared to the type of crown material.