Search

Composite resins are commonly used in dentistry for direct restorations. The color stability of these materials still represents a major concern for both the clinician and the patient. In recent years, ozone therapy has been extensively used in dentistry to manage wounds healing, dental caries, oral lichen planus, gingivitis and periodontitis, halitosis, osteonecrosis of the jaw, post-surgical pain, plaque and biofilms, root canal treatment, dentin hypersensitivity, temporomandibular joint disorders, and teeth whitening. To date, several studies have evaluated the bleaching effect exerted by ozone on natural teeth, but no studies have been conducted to determine the effect on the color of composite resins. The aim of the present study is to determine whether ozonized oils/gels could determine a color change on composite resin. A total of 40 discs of an A3 shade restorative composite were divided into two groups, respectively exposed to a pigmentation treatment consisting of 10 applications of 10 min each of a 1% chlorhexidine-based gel (trial group) and to storage into physiological solution (control group). The samples of both groups were respectively subdivided into four subgroups which underwent four different protocols, three of which were based on the exposure to different ozonized products and the latter representing the control. A colorimetric analysis with the CIELAB method was conducted with the following timing: after 24 h of storage in physiological solution (before the experimental procedures) (T0), after the subdivision into groups A and B (corresponding to the pigmentation for samples of group A and storage in physiological solution for samples of group B) (T1), and after subdivision into subgroups 1–4 (corresponding to the application of the ozonized products vs. control) (T2). No statistically significant difference was found between the samples at T0. The 20 samples of group A, exposed to the colorant agent, underwent a color change from T0 to T1, whereas the 20 samples exposed to the physiologic solution did not undergo any significant color change. A positive but moderate influence was assessed for E and L values, whereas no significant change occurred for A and B values. Therefore, dental ozonized oils/gels could be valuable in restorative dentistry as bleaching agents of resin composites exposed to discoloration, an alternative to the traditional hydrogen peroxide and carbamide peroxide, but further studies are required to confirm these findings. [ABSTRACT FROM AUTHOR]

The aim of the present in vitro study was to evaluate the protective effect of self-assembling peptide P11-4 (Curodont™ Protect/Credentis) on enamel erosion produced by a soft-drink, by using Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM). Thirty human incisors were equally and randomly assigned to 6 groups. Group 1: intact enamel, group 2: soft drink, group 3: Curodont™ Protect applied, group 4: Curodont™ Protect applied + soft drink, group 5: soft drink + Curodont™ Protect applied, group 6: soft drink + Curodont™ Protect applied + soft drink. Specimens were observed through atomic force microscopy (AFM). The root mean-square roughness (Rrms) was obtained from the AFM images and the differences in the averaged values among the groups were analyzed by Shapiro-Wilk test in order to assess the normality of the distribution. Parametric ANOVA and post hoc Tuckey test were performed to assess the differences between the different groups. After demineralization process, enamel demonstrated a high degree of surface porosity. This morphological aspect was reflected in the increase of Rrms values. No significant differences (p > 0.05) were reported between intact enamel and enamel only treated with P11-4 and between eroded enamel and enamel treated with P11-4 and then demineralized. However significant differences (p < 0.05) were recorded when comparing softened enamel with softened enamel further remineralized with biomimetic self-assembling peptides and enamel treated with the protective paste between two acid attacks. The use of P11-4 remineralizing may offer a degree of protection from enamel erosion. SCANNING 38:344-351, 2016. © 2015 Wiley Periodicals, Inc. [ABSTRACT FROM AUTHOR]

The aim of this study was to investigate the in vitro effect of a casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) paste (GC Tooth Mousse- TM, GC Corporation, Tokyo, Japan) on preventing enamel erosion, by using Atomic Force Microscopy (AFM). 30 human incisors, were equally assigned to 6 groups: intact enamel, enamel + soft drink, enamel + TM, enamel + TM + soft drink, enamel + soft drink + TM, enamel + soft drink + TM + soft drink. Specimens were observed through atomic force microscopy (AFM). The most common topographical parameters were determined, such as the surface roughness (Rrms). The use of soft drink on intact enamel has roughened the surface of the sample. The application of the CPP-ACP paste on non-treated enamel made the surface smoother. A significant decrease in roughness was seen after remineralization with CPP-ACP paste. Significant differences were recorded when comparing softened enamel with softened enamel remineralized with CPP-ACP paste. Comparing eroded enamel with demineralized/remineralized specimens, the application of a CPP-ACP paste leads to a significant reduction in roughness values. AFM images of enamel surface treated with CPP-ACP resulted in less morphological changes of the tooth substrate when compared with the only eroded enamel surface morphology; thus, indicating that CPP-ACP paste promoted remineralization. Specimens' surface roughness remained similar regardless that the protective agent is used before or after exposure to coke or between two demineralizing cycles. The results confirmed the effectiveness of the CPP-ACP paste on preventing enamel erosion produced by soft drinks. SCANNING 37:327-334, 2015. © 2015 Wiley Periodicals, Inc. [ABSTRACT FROM AUTHOR]