Search

Objectives: This study assessed the effects of blue and Er:YAG lasers, fluoride varnish, and their combination on microhardness, and calcium and phosphorus content of demineralized enamel. Materials and Methods: The primary Vickers microhardness of 28 third molars was measured and their enamel calcium and phosphorous content was quantified by energy-dispersive X-ray spectroscopy. They were then randomly assigned to five groups of 5% sodium fluoride (NaF) varnish, 445nm blue laser, Er:YAG laser, 5% NaF + 445nm blue laser, and 5% NaF + Er:YAG laser. The teeth then underwent pH-cycling to induce caries-like lesions. The surface microhardness of the teeth and the calcium and phosphorous content of demineralized enamel were measured again. Data were analyzed by one-way ANOVA and Tukey’s test (alpha=0.05). Results: NaF, NaF-diode laser, and NaF-Er:YAG laser groups experienced a significant increase in microhardness of demineralized enamel close to the baseline value (P

Introduction: In recent years, tooth whitening has become one of the most popular ways of achieving the original tooth color. The effect of whitening gel can be improved through heat, light or laser. The bond strength between the enamel and the composite can be reduced through bleaching and laser radiation. The purpose of this study is to assess the shear bond strength of resin composite to enamel after a bleaching process using hydrogen peroxide, with and without a laser (970 nm and 445 nm lasers). Method: This study used 51 extracted anterior teeth without caries that were divided into three groups. A 40% hydrogen peroxide gel was used on the enamel of all teeth. The control group received bleaching without a laser. Both the second and third treatment groups received bleaching with a laser, one with 970 nm and the other with 445 nm. After the bleaching process, all groups had etching, bonding and curing of the composite performed. Lastly, the shear bond strength between the enamel and the composite was measured and the failure modes were recorded. The data were compared using a one-way ANOVA test. Results: The mean shear bond strength between the enamel and the composite in the 445 nm group three (445 nanometer) was significantly lower than the other groups (p < 0.05). There was no significant difference between the control and the 970 nm groups (p = 0.2). Conclusion: According to the laser wavelengths and parameters that were used in this study and the results of this study, office bleaching with a 445 nm laser weakened the shear bond strength between the enamel and the composite.

Objectives: The aim of this study was to assess the microtensile bond strength of three universal adhesives to dentin and enamel. Materials and Methods: Sixty extracted human third molar teeth were chosen and divided into six groups regarding the adhesive (G-Premio Bond, Clearfil S3 Bond or Single Bond) and tooth surface. All the applied bonding agents were universal adhesives. The teeth were polished and the adhesives were applied; then the teeth were restored with composite resin. The samples were mounted in acrylic resin and sectioned. The specimens were subjected to a universal testing machine and the microtensile bond strength was measured. The failure mode of each specimen was determined under a stereomicroscope. Data were analyzed using two-way ANOVA (α=0.05). Results: The microtensile bond strength of G-Premio Bond to enamel and dentin was 11.79±8.27 and 17.55±9.47 MPa, respectively which was not significantly different from the values in Single Bond group (15.59±10.66 and 17.19±10.09 MPa to enamel and dentin, respectively; P>0.05). However, the values for Clearfil S3 Bond were 7.11±4.23 and 7.88±8.83 MPa to enamel and dentin, respectively, which were significantly lower than the values for G-Premio Bond (P