Search

The aim of this study was to evaluate the effect of 2% chlorhexidine digluconate (CHX) on microtensile bond strength (µTBS) between an adhesive system and under 3 dentin conditions. For that, this study evaluated the adhesive interface at initial, after 6 months and 1 year of storage. Forty-eight human third molars were prepared and randomly divided into 3 groups, according to dentin substrates: sound dentin (Sd), caries-infected dentin (Ci) and caries-affected dentin (Ca). The groups were subdivided into two according to the dentin pre-treatment: application of 2% CHX or without pre-treatment (control). The dentin surfaces were etched with 35% phosphoric acid gel and bonded with Adper Single Bond 2 (3M ESPE) adhesive system according to manufacturer's instructions. Subsequently, the specimens were stored in deionized water at 37°C for 24h, 6 months and 1 year. Two additional teeth were used to analyze the bonding interfaces by SEM. Data was submitted to three-way ANOVA in a split plot design and Tukey's test (α = 0.05). The results showed that Ci decreased µTBS values when compared to Ca and Sd, regardless storages time or treatment. Stored samples for 6 months and 1 year decreased the µTBS for the control group, but no difference was found between storages time for the CHX group. As a conclusion, the 2% CHX application after etching showed improved dentin bond strength in the storage time, regardless of the substrates evaluated.

The purpose of this study was to evaluate the influence of various concentrations of hydrofluoric acid (HF) on the surface/interface morphology and μ-shear bond strength (μSBS) between IPS Empress Esthetic (EST) (Ivoclar Vivadent) and IPS e.max Press (EMX) (Ivoclar Vivadent) ceramics and resin cement. Ceramic blocks were divided into 12 groups for each kind of ceramic. Six different HF concentrations were evaluated: 1%, 2.5%, 5%, 7.5%, 10%, and 15%. All groups were silanated after etching, and half of the specimens within each group received a thin layer of unfilled resin (UR). Three resin cement cylinders were prepared on each ceramic block for μSBS testing. The specimens were stored in distilled water at 37°C for 24 hours. The μSBS test was carried out in a universal testing machine at a crosshead speed of 0.5 mm/min until fracture. The data were submitted to three-way analysis of variance and multiple comparisons were performed using the Tukey post hoc test (p<0.05). The etched surfaces and bonded interfaces were evaluated using scanning electron microscopy. μSBS means (MPa) for 1%, 2.5%, 5%, 7.5%, 10%, and 15% HF concentrations were, respectively, 25.2, 27.2, 30.1, 31.4, 33.3, and 31.8. μSBS means with or without UR application measured 32.24 and 27.4, respectively; EST and EMX measured 29.8 and 29.9, respectively. For the HF concentrations, 10% and 15% showed higher μSBS means than did 1% and 2.5% (p<0.05); 7.5% was higher than 1% (p<0.05); and no statistical differences were found among the other concentrations (p>0.05). When evaluating UR, μSBS mean was significantly higher and better infiltration was observed on the etched surfaces. No statistical difference was found between the ceramics. The HF concentration and UR influenced the bond strength and surface/interface morphology.

The combined use of silane and solvated bonding agents on the bond strength to glass-fibre posts was investigated. A model Bis-GMA/HEMA adhesive was formulated with no solvent, 30% of ethanol or 80% of acetone. The surfaces of rectangular-shaped posts were silanated or not and one of the agents was applied, except for the control group. Cylinders of resin cement (RelyX ARC, 3M ESPE, Saint Paul, MN, USA) were built-up on the surfaces (n = 20) and submitted to shear testing. All groups showed higher bond strengths when the surfaces were silanated. When no silanization was carried out, the use of bonding agents, either solvated or non-solvated, increased the bond strengths. All groups treated with both silane and bonding agent showed higher bond strengths than the group that was only silanated. Control and ethanol-based adhesives were similar, whereas the acetone-based agent yielded higher bond strengths. Adhesive failures were predominant. Combination of silane and adhesive enhanced the bond to fibre posts., (© 2011 The Authors. Australian Endodontic Journal © 2011 Australian Society of Endodontology.)

This study focused on adhesive interface morphologic characterization and nanoleakage expression of resin cements bonded to human dentin pretreated with 1% chlorhexidine (CHX). Thirty-two non-carious human third molars were ground flat to expose superficial dentin. Resin composite blocks were luted to the exposed dentin using one conventional (RelyX ARC) and one self-adhesive resin cement (RelyX U100), with/without CHX pretreatment. Four groups (n = 8) were obtained: control groups (ARC and U100); experimental groups (ARC/CHX and U100/CHX) were pretreated with 1% CHX prior to the luting process. After storage in water for 24 h, the bonded teeth were sectioned into 0.9 × 0.9 mm(2) sticks producing a minimum of 12 sticks per tooth. Four sticks from each tooth were prepared for hybrid layer evaluation by scanning electron microscope analysis. The remaining sticks were immersed in silver nitrate for 24 h for either nanoleakage evaluation along the bonded interfaces or after rupture. Nanoleakage samples were carbon coated and examined using backscattered electron mode. Well-established hybrid layers were observed in the groups luted with RelyX ARC. Nanoleakage evaluation revealed increase nanoleakage in groups treated with CHX for both resin cements. Group U100/CHX exhibited the most pronouncing nanoleakage expression along with porous zones adjacent to the CHX pretreated dentin. The results suggest a possible incompatibility between CHX and RelyX U100 that raises the concern that the use of CHX with self-adhesive cements may adversely affect resin-dentin bond., (Copyright © 2013 Wiley Periodicals, Inc.)

Purpose: To evaluate the effect of two adhesive systems and different aging protocols on the bond strength of a -repaired microhybrid composite., Materials and Methods: Eighty test specimens (n = 20) and 10 control specimens measuring 8 x 4 mm were fabricated of a microhybrid composite (4 Seasons, shade A2) and grouped according to time/aging protocol: G1: 24 h in artificial saliva; G2: 7 days in artificial saliva; G3: 30 days in artificial saliva; G4: artificial accelerated aging (AAA) for 384 h; G5: control. After aging, samples were submitted to three types of surface treatment: SB2: Adper Single Bond 2, a two-step adhesive (3M ESPE); SB3: Adper Scotchbond Multi-Purpose, a three-step adhesive (3M ESPE); C: without application of adhesive (control). After this, test specimens were repaired with the same composite of a different shade (C3), and submitted to the microtensile test at a crosshead speed of 0.5 mm/min. Failure modes were analyzed by scanning electron microscopy (Jeol JSM 7500). Statistical analysis was performed using ANOVA and Tukey's test (p < 0.05)., Results: G2/SB2 presented significantly lower bond strength values in comparison with the other groups (p < 0.05). The control group presented the highest bond strength values, which differed statistically significantly from SB3, G3/SB2, and G4/SB2 (p < 0.05). Fractographic analysis demonstrated that most samples presented predominantly cohesive failures, excepting GI/SB2, which presented mixed and cohesive failures, and G4/SB2 and G1/SB3, which showed adhesive failures., Conclusion: The repair was more effective when performed after a short period of time and when the 3-step adhesive system (SB3) was used.

Purposes: This study evaluated the effect of gamma radiation on the microtensile bond strength of resin-based composite restoration to human enamel and dentin performed either before or after radiotherapy., Methods: Thirty sound human third molars were sectioned mesio-distally into buccal and lingual halves and then randomly divided into enamel or dentin groups. Enamel and dentin substrates were randomly divided into three sub-groups (n = 10): Control, which received no irradiation; specimens were irradiated before restoration protocol; and specimens were irradiated after restoration protocol. Radiation therapy was defined by application of 60-Gy dose fractionally with daily exposures of 2 Gy, 5 days a week, over 6 weeks. Restorations were carried out using Adper Single Bond adhesive system and Filtek Z250 resin composite. The specimens were sectioned producing 4 sticks per specimen and submitted to microtensile on a testing machine. Data were submitted to two-way ANOVA followed by Tukey test (p < 0.05). Failure modes were examined under optical microscopy and SEM., Results: Bond strength to enamel was significantly higher than to dentin irrespective radiation therapy. Radiotherapy applied before restoration significantly reduced the bond strength to both substrates. A predominance of adhesive failures was detected for control groups and groups restored before radiotherapy. Cohesive failures in dentin and enamel increased when the specimens were restored after irradiation., Conclusions: The gamma radiation had a significant detrimental effect on bond strength to human enamel and dentin when the adhesive restorative procedure was carried out after radiotherapy.

The aim of the study was to evaluate the bond strength of fibre glass and carbon fibre posts in the root canal walls cemented with self-adhesive (RelyX-Unicem) and chemical (Cement-Post) resin cements. Forty maxillary canines were divided into four groups according to the cement and post used and submitted to the push-out test (0.5 mm min(-1)). The data were submitted to statistical analysis (2-way ANOVA, Bonferroni--P<0.05) and fracture analysis by Scanning Electronic Microscopy. Fibre glass presented the best results when cemented with RelyX-Unicem and Cement-Post (P<0.05). RelyX-Unicem presented the highest bond strength values for both posts (P<0.05). Fracture analysis showed predominance of cohesive fracture of post for RelyX-Unicem and adhesive fracture between dentin/cement and mixed for Cement-Post. The bond strength values were significantly affected by the type of post and cement used and the highest values were found for fibre glass posts and RelyX-Unicem., (© 2010 The Authors. Australian Endodontic Journal © 2010 Australian Society of Endodontology.)

Purpose: The aim of the study was to assess the in vitro bond strength (BS) of glass fiber posts (GF) and carbon fiber posts (CF) in the cervical, middle, and apical thirds of root canals cemented with RelyX-Unicem (RX) and Cement-Post (CP)., Materials and Methods: Forty maxillary canines were divided into 4 groups (n = 10) according to the cement and post used: group 1: GF and RX; group 2: CF and RX; group 3: GF and CP; group 4: CF and CP. The push-out test was applied in the cervical, middle and apical thirds of each specimen to assess bond strength of the cement/post complex to the root canal wall. The data obtained were submitted to ANOVA (Bonferroni test, p < 0.05), and fracture analysis was done with SEM., Results: The GF posts presented the best results when cemented with RX and with CP (p < 0.05). RX presented the highest BS values for both GF and CF (p < 0.05). For all the groups, BS was higher in the cervical third, followed by the middle and apical thirds. Fracture analysis showed a predominance of cohesive fracture of posts for RX, and a predominance of adhesive fracture between dentin/cement, and mixed failure mode for CP., Conclusion: GF posts cemented with RX presented the highest BS values in all root thirds.

The aim of this study was to assess bond strength of fiberglass posts to root canal dentin irradiated with a 980 nm diode laser at different parameters of power and frequency. Fifty human maxillary canines were separated into five groups (n = 10) according to the following parameters of laser power and frequency: Group 1 (1.5 W/100 Hz), Group 2 (1.5 W/continuous wave [CW]), Group 3 (3.0 W/100 Hz), Group 4 (3.0 W/CW), and Group 5 (no irradiation). Following post cementation, samples underwent a push-out test (0.5 mm/min); next, fracture analysis was performed with a light microscope at 50x and 100x magnification. All of the irradiated groups had increased bond strength values compared to the nonirradiated group. Groups 1 and 2 demonstrated the highest bond strength values; however, statistically significant differences were observed for only the cervical third of Group 4 and the cervical/apical thirds of Group 5. Fracture analysis showed a predominance of mixed failures for Groups 1 and 2 and adhesive failures between dentin and cement for the other groups.

Objective: To assess the bond strength of Rely-X Unicem (RX), in comparison with Cement-Post (CP), to the cervical, middle and apical thirds of root canal dentin irradiated with a 980-nm diode laser., Material and Methods: Forty maxillary canines were separated into four equal groups according to the cement used and the laser surface treatment: RX/laser irradiation (LI) group; RX/no irradiation (NI) group; CP/LI group; and CP/NI group. Two slices (2-mm thick) of each root third were submitted to a push-out test to assess the bond strength of the cement to the root canal dentin. The data obtained were submitted to two-way ANOVA and fracture analysis was performed by scanning electron microscopy., Results: The type of cement as well as 980-nm LI at the different root canal thirds significantly affected the bond strength values (p < 0.05). LI promoted an increase in bond strength of RX in all root thirds (p < 0.05). For all groups, bond strength to the cervical third was highest, followed by the middle and apical thirds (p < 0.05). When the cements were compared, RX always presented the highest bond strength in comparison with CP, irrespective of the laser application (p < 0.05). Fracture analysis showed a predominance of mixed failures for RX and of adhesive failure between dentin and cement for CP, irrespective of the laser application., Conclusion: The 980-nm LI promoted an increase in bond strength of the self-adhesive resinous cement to root dentin.