Search

Statement of Problem: With a number of zirconia ceramic materials currently available for clinical use, an overview of the scientific literature on the adhesion methods and their potential influence is indicated., Purpose: The purpose of this systematic review was to classify and analyze the existing methods and materials proposed to improve adhesion to zirconia surfaces., Material and Methods: The current literature of in vitro studies examining the bond strength on zirconia ceramics, including clinical studies from 1998 until 2014, was analyzed. A search of the English language literature was undertaken using MEDLINE and PubMed, and a hand search was made for any relevant research paper from the library of a dental school. Papers evaluating only alumina restoration bond or ceramic-zirconia bond were excluded., Results: A total of 134 publications were identified for analysis. Different adhesive techniques with different testing methods were reviewed. Results were difficult to compare in that the parameters varied in each research protocol., Conclusions: Airborne-particle abrasion and tribochemical silica coating are reference pretreatment methods. Adhesive monomers are necessary for chemical bonding. Surface contamination and aging have negative effects on adhesion to zirconia. Many factors influence each combination of zirconia material, such as surface treatment, adhesive medium, and aging conditions. Laboratory studies should be confirmed by clinical trials., (Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.)

Purpose: This laboratory study compared the effect of different surface treatments of a medium-gold, high-noble alloy on the shear bond strength of an indirect, highly filled resin composite to the alloy and on the elemental composition of the alloy surface., Materials and Methods: Ninety disks, cast in a medium-gold, high-noble porcelain-fused-to-metal alloy (V-Deltaloy), received three different surface treatments: sandblasting with 50-microm Al2O3 (group 1) or 250-microm Al2O3 (group 2) and chemical agents, or with 250-microm Al2O3 without chemical agents (group 3) prior to bonding of an indirect resin composite (Artglass, and chemical agents Siloc-pre and Siloc-bond). The specimens were tested in shear, half of them after 24-hour dry storage at room temperature and the rest after 10-day storage in normal saline solution at 37 degrees C and thermocycling (2,500 cycles between 5 and 55 degrees C). Morphologic and qualitative changes on the alloy surface after sandblasting with 50- or 250-microm Al2O3 were examined by SEM using EDS analysis and compared with polished specimens. Statistical analysis was performed using two-factor ANOVA., Results: The mean shear bond strengths (in MPa) after dry or wet storage and thermocycling were 29 and 24 for group 1, 21 and 18 for group 2, and 17 and 12 for group 3, respectively; there was a statistically significant difference among the groups. Sandblasting of the alloy surface led to statistically significant changes in elemental composition. These changes were of greater magnitude when 50-microm Al2O3 particles were used., Conclusion: The particle size used for sandblasting influences the shear bond strength between a high-noble alloy and a highly filled indirect resin composite, as well as the elemental composition of the alloy surface.

Purpose: This laboratory study compared the shear bond strength between three indirect resin composites and a noble alloy using their respective bonding systems., Materials and Methods: One hundred twenty disks cast in a medium-gold, high-noble metal-ceramic alloy (V-Deltaloy) were divided equally into four groups and received different treatments for veneering: Conventional feldspathic porcelain (Omega) was applied on one set of specimens to be used as a control, and three indirect resin composites (Artglass, Sculpture, Targis) with their respective bonding systems were used for the other groups. The specimens were tested in a parallel shear test, half of them after 24-hour dry storage at room temperature and the rest after 10-day storage in normal saline solution at 37 degrees C and thermocycling. The fractured specimens were evaluated to determine the nature of the failure., Results: The mean shear bond strength values (in MPa), before and after wet storage and thermocycling, were 30 and 23 for the metal-ceramic group, 29 and 23 for the Artglass group, 20 and 19 for the Sculpture group, and 17 and 14 for the Targis group, respectively. The metal-ceramic and Artglass groups exhibited significantly higher bond strengths than the other two groups. All specimens, with the exception of the Sculpture group, showed a significant decrease in bond strength after wet storage and thermocycling., Conclusion: No group exceeded the shear bond strength of the metal-ceramic group, but the Artglass group with its respective metal-resin bonding system exhibited similar bond strengths. The Sculpture group showed a stable bond after water storage and thermocycling.