Search

Objective: Dentinal MMPs have been claimed to contribute to the auto-degradation of collagen fibrils within incompletely resin-infiltrated hybrid layers and their inhibition may, therefore, slow the degradation of hybrid layer. This study aimed to determine the contribution of a synthetic MMPs inhibitor (galardin) to the proteolytic activity of dentinal MMPs and to the morphological and mechanical features of hybrid layers after aging., Methods: Dentin powder obtained from human molars was treated with galardin or chlorhexidine digluconate and zymographically analyzed. Microtensile bond strength was also evaluated in extracted human teeth. Exposed dentin was etched with 35% phosphoric acid and specimens were assigned to (1) pre-treatment with galardin as additional primer for 30s and (2) no pre-treatment. A two-step etch-and-rinse adhesive (Adper Scotchbond 1XT, 3M ESPE) was then applied in accordance with manufacturer's instructions and resin composite build-ups were created. Specimens were immediately tested for their microtensile bond strength or stored in artificial saliva for 12 months prior to being tested. Data were evaluated by two-way ANOVA and Tukey's tests (alpha=0.05). Additional specimens were prepared for interfacial nanoleakage analysis under light microscopy and TEM, quantified by two independent observers and statistically analyzed (chi(2) test, alpha=0.05)., Results: The inhibitory effect of galardin on dentinal MMPs was confirmed by zymographic analysis, as complete inhibition of both MMP-2 and -9 was observed. The use of galardin had no effect on immediate bond strength, while it significantly decreased bond degradation after 1 year (p<0.05). Interfacial nanoleakage expression after aging revealed reduced silver deposits in galardin-treated specimens compared to controls (p<0.05)., Conclusions: This study confirmed that the proteolytic activity of dentinal MMPs was inhibited by the use of galardin in a therapeutic primer. Galardin also partially preserved the mechanical integrity of the hybrid layer created by a two-step etch-and-rinse adhesive after artificial aging., (Copyright (c) 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.)

Purpose: The aim of this study was to investigate whether an electrical device for dental adhesive application (ElectroBond) influences bonding of two-step etch-and-rinse adhesives., Materials and Methods: Human teeth were selected and cut perpendicularly to their long axis to expose middle/ deep dentin. Specimens were then longitudinally sectioned into halves (experimental and control halves) to create two similar bonding substrates. Experimental halves were bonded using an ElectroBond-assisted application, while control halves were bonded with disposable sponges. The adhesives tested were Adper Scotchbond 1XT and XP-BOND. Bonded specimens were submitted to the microtensile bond strength test. Additional adhesive interfaces were prepared and processed for nanoleakage investigation involving TEM examination., Results: The microtensile bond test revealed higher values (p < 0.05) for both adhesives if ElectroBond was used during layering (55.5 +/- 7.9 MPa for Adper Scotchbond 1XT and 54.7 +/- 7.1 MPa for XP-BOND) compared to the conventional mechanical adhesive application technique (41.1 +/- 6.1 MPa for Adper Scotchbond 1XT and 38.0 +/- 7.8 MPa for XP-BOND). No difference between the two adhesives was found under the same application conditions. With electricity-assisted application, TEM micrographs revealed a significant decrease in nanoleakage expression compared to the controls., Conclusion: The use of an electric current produced by ElectroBond during the application of two-step etch-and-rinse adhesives may enhance resin impregnation, thus improving dentin hybridization. Further studies should be done to confirm that this device can similarly improve adhesive application in vivo.

Objective: Most of current dental adhesive systems show favorable immediate results in terms of retention and sealing of bonded interface, thereby counteracting polymerization shrinkage that affects resin-based restorative materials. Despite immediate efficacy, there are major concerns when dentin bonded interfaces are tested after aging even for short time period, i.e. 6 months., Methods: This study critically discusses the latest peer-reviewed reports related to formation, aging and stability of resin bonding, focusing on the micro and nano-phenomena related to adhesive interface degradation., Results: Most simplified one-step adhesives were shown to be the least durable, while three-step etch-and-rinse and two-step self-etch adhesives continue to show the highest performances, as reported in the overwhelming majority of studies. In other words, a simplification of clinical application procedures is done to the detriment of bonding efficacy. Among the different aging phenomena occurring at the dentin bonded interfaces, some are considered pivotal in degrading the hybrid layer, particularly if simplified adhesives are used. Insufficient resin impregnation of dentin, high permeability of the bonded interface, sub-optimal polymerization, phase separation and activation of endogenous collagenolytic enzymes are some of the recently reported factors that reduce the longevity of the bonded interface., Significance: In order to overcome these problems, recent studies indicated that (1) resin impregnation techniques should be improved, particularly for two-step etch-and-rinse adhesives; (2) the use of conventional multi-step adhesives is recommended, since they involve the use of a hydrophobic coating of nonsolvated resin; (3) extended curing time should be considered to reduce permeability and allow a better polymerization of the adhesive film; (4) proteases inhibitors as additional primer should be used to increase the stability of the collagens fibrils within the hybrid layer inhibiting the intrinsic collagenolytic activity of human dentin.

Purpose: This study evaluated the marginal microleakage in bonded amalgam restorations in teeth extracted a month after restoration placement., Materials and Methods: Nine teeth in a patient scheduled for complete extraction were selected. In each tooth, a buccal prepared cavity was treated with Scotchbond Plus and filled with high copper amalgam. In four teeth, a lingual unlined restoration was also prepared as control. A month later, all the teeth were extracted; seven teeth were immersed for 48 hours in a 0.05% basic fucsine dye solution and then sectioned. Sections were observed with a stereomicroscope at 10X. Results were statistically evaluated using a nonparametric Mann-Whitney test for independent data. The remaining two teeth were sectioned and observed using a scanning electron microscope (SEM)., Results: Stereomicroscopic analysis revealed that 80% of bonded specimens did not exhibit dye infiltration at the enamel margin; the same percentage of bonded specimens showed partial infiltration at the cervical margin. In the unlined control specimens, there was a complete dye infiltration at both margins. SEM analysis revealed a good adaptation between resin and tooth and between resin and amalgam., Conclusion: Bonded amalgam restorations are effective in reducing marginal microleakage, particularly at the enamel margin.