Search

The non‐radiative recombination at the interfaces of perovskite solar cells (PSCs) is a crucial issue that limits the efficiency and stability of the devices. State‐of‐the‐art surface passivation strategies usually utilize alkyl ammonium halides to suppress the non‐radiative recombination of PSCs, but their high surface reactivity leads to the transformation into 2D perovskites under working conditions, limiting the passivation effect and the charge transport of PSCs. Herein, a non‐halide ionic salt 1‐naphthylmethylammonium formate (NMACOOH) is synthesized for surface passivation of perovskite films. In contrast to the traditional 1‐naphthylmethylammonium iodide, NMACOOH treatment hinders the formation of 2D perovskite and forms a thermally stable PbI2‐NMACOOH adduct on the perovskite surface. Surface characterization reveals that NMA+ can passivate the cation vacancies of the 3D perovskite while HCOO− passivates the metallic Pb0 and halide‐vacancy defects. Therefore, the non‐radiative recombination of PSCs is dramatically suppressed and a high open‐circuit voltage of 1.19 V is obtained. Finally, PSCs with high efficiency of 24.75% and improved long‐term stability (98% of the initial efficiency after 1800‐h storage) are obtained. Moreover, the NMACOOH‐passivated devices also show robust operational stability, retaining 83% of the initial efficiency after working for 658 h under continuous one‐sun illumination. [ABSTRACT FROM AUTHOR]

The under‐coordinated defects within perovskite and its relevant interfaces always attract and trap the free carriers via the electrostatic force, significantly limiting the charge extraction efficiency and the intrinsic stability of perovskite solar cells (PSCs). Herein, self‐diffusion interfacial doping by using ionic potassium L‐aspartate (PL‐A) is first reported to restrain the carrier trap induced recombination via the reconstruction of energy level structure at SnO2/perovskite interface in conventional n‐i‐p structured PSCs. Experiments and theories are consistent with the PL‐A anions that can remain at the SnO2 surface due to strong chemical adsorption. During the spin‐coating of the perovskite film, the cations gradually diffuse into perovskite and endow an n‐doping effect, which provides higher force and a better energy level alignment for the carrier transport. As a result, they obtained 23.74% power conversion efficiency for the PL‐A modified small‐area devices, with dramatically improved open‐circuit voltage of 1.19 V. The corresponding large‐area devices (1.05 cm2) achieved an efficiency of 22.23%. Furthermore, the modified devices exhibited negligible hysteresis and enhanced ambient air stability exceeding 1500 h. [ABSTRACT FROM AUTHOR]

Designing functional fullerenes with roles beyond defect passivation and electron‐transporting for perovskite solar cells (PSCs) is essential to the development of fullerenes and PSCs. Here, the authors design and synthesize a functional fullerene, FPD, composed of a C60 cage, a porphyrin ring, and three pentafluorophenyl groups. The structure features of FPD enable it can form chemical interactions with the perovskite lattices. These interactions enhance the defect passivation effect and prevent the decomposition of perovskite under irradiation. As a result, the FPD‐based device yields an improved power conversion efficiency of 23% with substantially enhanced operational stability (T80 > 1500 h). Furthermore, once got damaged, the FPD can prevent lead leakage by forming a stable and water‐insoluble complex (FPD‐Pb). Their findings provide a novel strategy to achieve high‐performance and eco‐friendly PSCs with functional fullerene materials. [ABSTRACT FROM AUTHOR]

It is challenging to passivate defects that are buried in the depth of perovskite films; most of the reported passivation methods cannot reach the deep defects. Herein, methanol is adopted as a dual‐functional reagent to not only act as a solvent but also help the dissolved ions penetrate the depth of perovskite films. By treating the as‐prepared perovskite films with CsBr/methanol solution, Br− ions can react with the undercoordinated Pb2+, and Cs+ ions can fill in the cation vacancies. This strategy enables surface and bulk defects passivation to be achieved simultaneously. The nonradiative recombination of the double‐passivated devices is significantly suppressed and the migration of charged defects is remarkably hindered. As a result, an improved power conversion efficiency of 19.5% and an open‐circuit voltage of 1.183 V is achieved. Moreover, the passivated device can retain ≈80% of the initial efficiency after working for 500 h at maximum power point under 1‐sun illumination, whereas the pristine device reaches 80% of the initial efficiency after only 90 h. This work demonstrates that surface and bulk defects passivation is critical to improve the efficiency and long‐term operational stability of the perovskite solar cells. [ABSTRACT FROM AUTHOR]