Abstract: The collective influence of crucial electrodeposition parameters (temperature, deposition voltage and bath composition) on the properties of Zn–Ni films electrodeposited in a choline chloride–urea eutectic-based ionic liquid was investigated. The microstructures, chemical compositions, phase structures and corrosion behaviors of electrodeposited films were analyzed using scanning electron microscope, energy dispersive X-ray spectroscopy, X-ray diffraction and linear cyclic voltammetry, respectively. The surface morphologies and chemical compositions of the films were strongly dependent on the electrodeposition parameters. It was found that the amounts of nickel in the Zn–Ni alloy films were significantly higher than that present in the electrolytes and was always above 50%, indicating normal codeposition mechanism. Electrodeposition of high Zn content alloy is favorable at high electrodeposition voltages, high temperatures and high Zn (II)/Ni (II) ratios. Electrochemical measurements shows that under the conditions considered, the Zn–Ni film from 0.45M Zn (II)–0.05M Ni (II) deposited at 55°C and 0.8V exhibits the highest barrier corrosion resistance compared with the other films and this was attributed to a dense, smooth and crack free morphology with optimum Zn content. [Copyright &y& Elsevier]

Abstract: Pure Ni and three Ni–Co alloys films, i.e. Ni–4wt.%Co, Ni–18wt.%Co, and Ni–40wt.%Co, are electrodeposited at room temperature from the choline chloride/ethylene glycol deep eutectic solvent dissolved by nickel or/and cobalt chlorides. Electrodeposition mechanism, microstructure, and corrosion properties of the films are investigated. Surface morphology and chemical composite of the films are significantly dependent on the Ni2+ and Co2+ concentrations in the electrolytes. Interestingly, it is found that the amount of cobalt in the Ni–Co alloy films is significantly lower than that present in the electrolytes, which indicates an absence of anomalous codeposition process for the non-aqueous electrolytes. However, anomalous codeposition of Ni–Co deposits is frequently observed for the aqueous electrolytes. The Ni–Co alloy films possess face-centered cubic structures and refined grains revealed by X-ray diffractometer and scanning electron microscope. Potentiodynamic polarization measurements show that the Ni film exhibits the noblest corrosion potential and the lowest corrosion current compared with the Ni–Co alloys films. Moreover, the more Co content the Ni–Co films have, the more negative corrosion potential and the higher corrosion current the films exhibit. [Copyright &y& Elsevier]