Gambarini G, Gergi R, Naaman A, Osta N, Al Sudani D. Cyclic fatigue analysis of twisted file rotary NiTi instruments used in reciprocating motion. International Endodontic Journal, 45, 802-806, 2012. Abstract Aim To evaluate the cyclic fatigue fracture resistance of engine-driven twisted file (TF) instruments under reciprocating movement. Methodology A sample of 30 size 25, 0.08 taper NiTi TF instruments was tested in a simulated canal with 60˚ angle of curvature and a 3 mm radius. During mechanical testing, different movement kinematics were used at a constant speed, which resulted in three experimental groups (each group n = 10). The instruments from the first group (G1) were rotated until fracture occurred. The instruments in the second (G2) and third group (G3) were driven under reciprocating movement with different angles of reciprocation. The time of fracture for each instrument was measured, and statistical analysis was performed using one-way analysis of variance followed by Tukey's Honestly Significant Different test. Results Reciprocating movement resulted in a significantly longer cyclic fatigue life ( P < 0.0001) when compared with continuous rotation. No difference was found between reciprocation 150° clockwise/30° counterclockwise (CW/CCW) and 30° CW/150° CCW. Conclusions The reciprocating movement was associated with an extended cyclic fatigue life of the TF size 0.25, 0.08 taper instruments in comparison with conventional rotation. [ABSTRACT FROM AUTHOR]

Aim To investigate whether flexibility and cyclic fatigue resistance was increased for nickel-titanium instruments produced by a new manufacturing technique. Methodology Forty K3 tip size 25, 0.06 taper (SybronEndo) nickel-titanium rotary instruments were randomly selected and divided into two groups (n = 20). One group served as control, being the commercially available instruments produced with a traditional grinding process (K3). The second group of instruments (K4 prototypes) were then subjected to a proprietary thermal treatment after the grinding process. Finally, each group was randomly divided into two subgroups of 10 instruments each, to perform the stiffness test and the cyclic fatigue test. All data were recorded and subjected to statistical evaluation using Student's t-test. Significance was set at the 95% confidence level. Results For the stiffness test, a statistically significant difference (P < 0.05) was noted between K3 and K4 prototype instruments. K4 prototype instruments were significantly more flexible when compared to K3 instruments (59.3 ± 4.3 vs. 98.1 ± 6.4 g cm-1). For the cyclic fatigue test, a significant difference (P < 0.05) was noted between K3 and K4 prototype instruments. K4 prototype instruments demonstrated a significant increase in the mean number of cycles to failure (NCF) when compared to K3 instruments (1198 ± 279 vs. 542 ± 81 NCF). Conclusions The new manufacturing technique resulted in the K4 prototype instruments having enhanced mechanical properties, compared to K3 instruments, manufactured with a traditional grinding process. [ABSTRACT FROM AUTHOR]