In this work, TiC nanoparticles (TiCps) reinforced 7075 aluminium alloy was fabricated via an oscillating laser-arc hybrid additive manufacturing process. To show the beneficial effect of TiCps addition on microstructure and mechanical properties, a conventional 7075 aluminium alloy was also manufactured for comparison. Upon the addition of TiCps, remarkable grain refinement was achieved with a decrease in average grain size from 111.8 to 12.5 µm, and grain boundary segregation was alleviated. It was also found that many secondary phases precipitated at the grain interior in the deposit with TiCps. Owing to the refined microstructure and favourable precipitation, as-deposited 7075 aluminium alloy with TiCps showed enhanced tensile properties of ultimate tensile strengths of 346 and 355 MPa along scanning and build directions. [ABSTRACT FROM AUTHOR]

• The hot cracks are eliminated in the LPBF-processed ZK60. • The grain size is significantly reduced after the powders modified by Y. • The grain boundaries are strengthened by the I - phase. • The cracks in LPBF-processed ZK60 samples are attributed to the Mg 7 Zn 3. The hot cracks of laser powder bed fusion (LPBF) processed ZK60 components were eliminated by adding rare earth element Y. The cause of the cracks in the samples and the suppression mechanism were analyzed in detail. The cracks in ZK60 LPBF samples were mainly caused by the low-melting eutectic phase Mg 7 Zn 3 at the grain boundaries. The average grain size decreased from 7.2 μm to 2.0 μm after adding Y. The I-phase with excellent thermal stability strengthened the grain boundaries. The elimination of cracks was mainly attributed to the I-phase at the grain boundary and the grain refinement. [ABSTRACT FROM AUTHOR]