Search

Asphalt mixture modification with rubberised material frequently results in improved characteristics and extended service life in actual application. This research characterised the synergistic consequences of rubber modifiers (crumb rubber powder (CRP) and natural rubber latex (NRL)) and wax-based admixtures (Tough Fix Hyper (TFH)) on the performance of the asphalt mixture from the fracture energy and laboratory fracture resistance perspectives. Semicircular bending (SCB) and indirect tensile strength (ITS) tests were conducted to assess the fracture properties of the asphalt mixture samples. To prepare asphalt mixture samples, the wet method was utilised. Higher CRP levels resulted in greater strength and a longer time to attain peak force for both control and mixtures containing wax admixture, as determined by SCB. The interaction between the higher CRP or NRL content and the TFH additive enhanced the fracture resistance, indicating that the components are highly compatible. The 10L + TFH additive produced the highest fraction of energy, indicating a more significant improvement than the counterpart mixes containing the CRP modifier. In addition, incorporation of the CRP and NRL increased the fracture plastic zone (FPZ), resulting in increased fracture toughness. Therefore, the gradient of fracture toughness and fracture energy in the asphalt mix depends on the rubber type, content, and TFH. Although the higher CRP, NRL, and TFH improve the fracture energy and cracking resistance, they increase the crack initiation and propagation velocities, whereby the high bitumen stiffness makes the mixture more brittle than the control mixture. Caution should be exercised when selecting the content of rubber modifier and TFH for the asphalt pavements in low-temperature service. Also, there is a direct interconnection between fracture resistance and fracture energy in the mixtures containing CRP, NRL, and TFH. Such correlations can be used as the premise of predictive micro- and macro-models to evaluate mixture performance in terms of fracture resistance. [ABSTRACT FROM AUTHOR]

Moisture damage is one of the most frequent damages that occurs on asphalt pavements. The application of rubberized materials for asphalt is widely acceptable due to cost saving and environmentally friendly. The purpose of this study is to assess the performance of rubberized asphalt mixtures containing wax-based admixture, namely Tough Fix Hyper (TFH), in terms of moisture sensitivity and hazardous compound leaching potential. The moisture absorption, chemical immersion, and boiling water tests were used to assess the resistance to moisture damage on aggregate-binder bonding characteristics. Following that, the trend of moisture sensitivity was evaluated through an image analysis procedure. To simulate the environmental impact of leaching, the toxicity characterization leaching procedure (TCLP) test was adopted. The results showed that interaction between the crumb rubber or latex with TFH decreases the stripping value of the mixes significantly based on the chemical immersion test. Furthermore, the image analysis of the samples subjected to boiling water conditioning showed that pixels of asphalt samples without TFH, ranging from 524,949 to 472,346, decrease from 520,870 to 289,070, indicating that the asphalt remained coated area improved by 67.70–91.39%. The analysis of the leachate test revealed that the heavy metals, including arsenic (As), nickel (Ni), copper (Cu), chromium (Cr), vanadium (V), and cadmium (Cd), were not detected. However, zinc (Zn) was detected in the modified mixture, ranging from 0.05 to 0.114 mg/L, which lies within the allowable norm. In conclusion, the incorporation of crumb rubber and TFH in asphalt mixtures poses no environmental risk. • The performance of rubberized asphalt mixtures containing wax-based admixture was studied. • The moisture sensitivity was evaluated through an image analysis procedure. • The environmental impact of leaching was evaluated using TCLP test. • Samples subjected to boiling water indicated that the asphalt remained coated area improved within 68–92%. • The outcomes of the leachate test revealed that the incorporation of crumb rubber and wax admixture has no environmental risk. [ABSTRACT FROM AUTHOR]