Search

The aim of this work is to investigate the effects produced by polymicrobial biofilm (Porphyromonas gingivalis, Streptococcus mutans, Streptococcus sanguinis, and Streptococcus salivarius) on the corrosion behavior of titanium dental implants. Pure titanium disks were polished and coated with titanium nitride (TiN) and silicon carbide (SiC) along with their quarternized versions. Next, the disks were cultivated in culture medium (BHI) with P. gingivalis, S. mutans, S. sanguinis, and S. salivarius and incubated anaerobically at 37 °C for 30 days. Titanium corrosion was evaluated through surface observation using Scanning Electron Microscope (SEM) and Atomic Force Microscopy (AFM). Furthermore, the Ti release in the medium was evaluated by Inductively Coupled Plasma Mass Spectrometry (ICP-MS). SEM images showed that coated Ti disks exhibited lower corrosion compared to non-coated disks, except for the quartenized TiN. This was confirmed by AFM, where the roughness was higher in non-coated Ti disks. ICP showed that Ti levels were low in all coating disks. These results indicate that these SiC and TiN-based coatings could be a useful tool to reduce surface corrosion on titanium implant surfaces. [ABSTRACT FROM AUTHOR]

The effect of pH changes on the chemical durability of dental glass–ceramic materials was evaluated using weight loss and ion release levels. The hypothesis that increased pH changes will exhibit greater corrosion was investigated. The ion concentration was analyzed using inductively coupled plasma atomic emission spectrometer (ICP). The surface compositions were investigated using X-ray photoelectron spectroscopy (XPS). The surface morphologies were examined using scanning electron microscopy (SEM). Dental glass–ceramics were tested in constant immersion, 3-day cycling, and 1-day cycling with pH 10, pH 2, and pH 7 for 3, 15, and 30 days. The 1-d cycling group demonstrated the highest levels of weight loss compared with 3-d cycling and constant immersion. For the ion release, Si4+ and Ca2+ had the highest rates of release in 1-d cycling, whereas the Al3+ release rate with constant pH 2 was highest. The alteration/passivation layer that was formed on the surface of disks possibly prevented further dissolution of pH 10 corroded disks. XPS analysis demonstrated different surface compositions of corroded disks in pH 10 and pH 2. Si4+, K+, Na+, Al3+, and Ca2+ were detected on the surface of corroded pH 10 disks, whereas a Si4+ and P5+-rich surface formed on corroded pH 2 disks. SEM results demonstrated rougher surfaces for corroded disks in cycling conditions and pH 2 constant immersion. In conclusion, increased pH changes significantly promote the corrosion of dental glass–ceramic materials. [ABSTRACT FROM AUTHOR]

The effect of a novel silicon carbide (SiC) coating on the chemical durability of a fluorapatite glass-ceramic veneer was investigated by examining weight loss and ion release levels. The hypothesis that this novel coating will exhibit significant corrosion resistance was tested. Inductively coupled plasma atomic emission spectrometer (ICP) was used for ion concentration determination and scanning electron microscopy (SEM) for surface morphology analyses. Samples were immersed in pH 10 and pH 2 buffer solutions to represent extreme conditions in the oral cavity. Analyses were done at 15 and 30 days. The SiC coated group demonstrated significant reduction in weight loss across all solutions and time points (p < 0.0001). Ion release analyses demonstrated either a marginally lower or a significantly lower release of ions for the SiC-coated disks. SEM analysis reveals planarization of surfaces by the SiC-coated group. The surfaces of coated samples were not as corroded as the non-coated samples, which is indicative of the protective nature of these coatings. In conclusion, SiC is a novel coating that holds promise for improving the performance of ceramic materials used for dental applications. [ABSTRACT FROM AUTHOR]