1. The influence of Pd on the interfacial reactions between the Pd-plated Cu ball bond and Al pad.
- Author
-
Lin, Yu-Wei, Ke, Wun-Bin, Wang, Ren-You, Wang, I-Sheng, Chiu, Ying-Ta, Lu, Kuo-Chang, Lin, Kwang-Lung, and Lai, Yi-Shao
- Subjects
- *
COPPER alloys , *INTERFACIAL reactions , *PALLADIUM , *ALUMINUM , *THICKNESS measurement , *METAL bonding - Abstract
Abstract: The interfacial reactions of the Pd-plated Cu (Pd–Cu) ball bond and 4N Cu (Cu) ball bond on Al were investigated through PCT (Pressure Cooker Test) and HTST (High Temperature Storage Test) tests. The thickness of the interfacial Cu–Al IMC increases as the testing time increases. The Cu Al IMC growth rate was found to be slower in the Pd Cu ball bond than in the Cu ball bond. The growth of the IMC is diffusion-controlled during aging. During the test, the Pd diffuses from the interior of the Pd Cu ball toward the bond interface. FIB (Focus Ion Beam) studies show crack formation at the Cu Al IMC/Al interface in the Cu ball bond. During aging, the Pd-rich layer affected the interdiffusion between Cu and Al and may influence the IMC formation. The Pd Cu ball bond showed better bonding reliability than the Cu ball bond in all tests. [Copyright &y& Elsevier]
- Published
- 2013
- Full Text
- View/download PDF