The paper presents an analysis of the impact of plastic deformation using hydrostatic extrusion (HE) on the structural, mechanical and functional properties of pure copper for use as electrodes in the process of electro discharge machining (EDM). As part of the research, copper was subjected to the HE process with the maximum cumulative true strain equal to ɛcum = 3.89 obtained in 5 stages. The result was, a refinement of the microstructure with the grains elongated in the direction of extrusion, with a cross-sectional size of d2 = 228 nm. As the obtained material can be potentially used in the process of electro discharge machining, the copper specimens after the HE process were subjected to a comprehensive analysis to determine the mechanical, physical and functional properties of the material. A significant increase in strength (UTS) and yield strength (YS) of the HE-processed copper was obtained, reaching respectively UTS = 464 MPa and YS = 456 MPa at the maximum strain of ɛ = 3.89. Despite the clear strain-induced strengthening of the material, a very high electrical conductivity of not less than 97% was obtained. The electrodes made of copper after HE process have reduced erosion wear while maintaining a comparable or better quality of the machined surface. The best results were obtained for finish machining, where the electrical discharge wear was lower by 60% compared to the electrode made of non-processed copper. In addition, an improvement in the surface quality after the EDM process by 25% was observed when using the HE-processed electrodes. [ABSTRACT FROM AUTHOR]

The research presented in this paper concerns the influence of the rate of plastic deformation generated directly in the processes of severe plastic deformations on the microstructure and properties of three metals: copper, iron and zinc. The equal channel angular pressing (ECAP) method was used, and it was performed at a low plastic deformation rate of ∼ 0.04 s−1 . The high plastic strain rate was obtained using the hydrostatic extrusion (HE) method with the deformation rate at the level of ∼ 170 s−1 . For all three tested materials different characteristic effects were demonstrated at the applied deformation rates. The smallest differences in the mechanical properties were observed in copper, despite the dynamic recrystallization processes that occurred in the HE process. In Armco iron samples, dynamic recovery processes in the range of high plastic deformation rates resulted in lower mechanical properties. The most significant effects were obtained for pure zinc, where, regardless of the method used, the microstructure was clearly transformed into bimodal after the ECAP process, and homogenized and refined after the HE process. After the HE process, the material was transformed from a brittle state to a plastic state and the highest mechanical properties were obtained. [ABSTRACT FROM AUTHOR]