Search

Poly(lactide) (PLA) and poly(ethylene glycol) (PEG)-based hydrogels were prepared by mixing phosphate buffer saline (PBS, pH 7.4) solutions of four-arm (PEG-PLA)2-R-(PLA-PEG)2 enantiomerically pure copolymers having the opposite chirality of the poly(lactide) blocks. Dynamic Light Scattering, rheology measurements, and fluorescence spectroscopy suggested that, depending on the nature of the linker R, the gelation process followed rather different mechanisms. In all cases, mixing of equimolar amounts of the enantiomeric copolymers led to micellar aggregates with a stereocomplexed PLA core and a hydrophilic PEG corona. Yet, when R was an aliphatic heptamethylene unit, temperature-dependent reversible gelation was mainly induced by entanglements of PEG chains at concentrations higher than 5 wt.%. When R was a linker containing cationic amine groups, thermo-irreversible hydrogels were promptly generated at concentrations higher than 20 wt.%. In the latter case, stereocomplexation of the PLA blocks randomly distributed in micellar aggregates is proposed as the major determinant of the gelation process. [ABSTRACT FROM AUTHOR]

Abstract: Poly(lactic acid) (PLA) and poly(butylene adipate-co-terephthalate) (PBAT) are biodegradable aliphatic polyesters, which being semicrystalline and thermoplastic can be processed by conventional methods. Their blends give interesting materials for industrial packaging applications, due to their increased ductility as PBAT content increases. However, like many aliphatic polyesters, the PLA matrix degrades upon melt processing thus affecting the thermo-mechanical features of the blended material. In this work, we studied the effect of processing at high temperature on the molecular weight distribution, morphology, and thermo-mechanical properties of both homopolymers, as well as the PLA/PBAT 75/25 blend. Notably, different processing conditions were adopted in terms of temperature (range 150–200°C) and other relevant processing parameters (moisture removal and nitrogen atmosphere). Analysis of PLA/PBAT blends indicated that intermolecular chain reactions took place under strong degradative conditions of PLA, yielding PLA/PBAT mixed chains (copolymers). Increasing amounts of copolymers resulted in improved phase dispersion and increased ductility, as SEM and mechanical tests indicated. Conversely, reduced PLA degradation with less copolymer formation, afforded higher modulus materials, owing to poorer dispersion of the soft phase (PBAT) into the PLA matrix. [Copyright &y& Elsevier]

Abstract: New biodegradable–biocompatible amphiphilic block copolymers were prepared in good yields by SnOct2 catalyzed ring opening polymerization of ε-caprolactone initiated by monomethoxy-terminated poly(ethylene glycol) (MPEG). Coupling of the AB copolymers with hexamethylene diisocyanate afforded ABA (formally ABBA) block copolymers. Both AB and ABA copolymers were thoroughly characterized by IR and NMR spectroscopy, size exclusion chromatography, TGA and DSC thermal analysis. In particular, DSC measurements evidenced that the copolymer hydrophilic–lipophilic balance appreciably affected the state of adsorbed water. Polarized optical microscopy of bulk materials and pyrene fluorescence emission of polymer water solutions highlighted the copolymer tendency to phase separation and self-organization, respectively. Most of the prepared materials formed micelles in water and the copolymer structure appreciably affected their critical micellar concentration. In vitro cytocompatibility tests confirmed the low toxicity of the prepared polymeric materials which enhances their potential for biomedical applications. [Copyright &y& Elsevier]

In the perspective of producing a rigid renewable and environmentally friendly rigid packaging material, two comb-like copolymers of cellulose acetate (AC) and oligo(lactic acid) OLA, feeding different percentages of oligo(lactic acid) segments, were prepared by chemical synthesis in solvent or reactive extrusion in the melt, using a diepoxide as the coupling agent and were used as compatibilizers for poly(lactic acid)/plasticized cellulose acetate PLA/pAC blends. The blends were extruded at 230 °C or 197 °C and a similar compatibilizing behavior was observed for the different compatibilizers. The compatibilizer C1 containing 80 wt% of AC and 14 wt% of OLA resulted effective in compatibilization and it was easily obtained by reactive extrusion. Considering these results, different PLAX/pAC(100-X) compounds containing C1 as the compatibilizer were prepared by extrusion at 197 °C and tested in terms of their tensile and impact properties. Reference materials were the uncompatibilized corresponding blend (PLAX/pAC(100-X)) and the blend of PLA, at the same wt%, with C1. Significant increase in Young's modulus and tensile strength were observed in the compatibilized blends, in dependence of their morphologic features, suggesting the achievement of an improved interfacial adhesion thanks to the occurred compatibilization. [ABSTRACT FROM AUTHOR]