Abstract: Poly(lactic acid) (PLA) and poly(butylene adipate-co-terephthalate) (PBAT) are biodegradable aliphatic polyesters, which being semicrystalline and thermoplastic can be processed by conventional methods. Their blends give interesting materials for industrial packaging applications, due to their increased ductility as PBAT content increases. However, like many aliphatic polyesters, the PLA matrix degrades upon melt processing thus affecting the thermo-mechanical features of the blended material. In this work, we studied the effect of processing at high temperature on the molecular weight distribution, morphology, and thermo-mechanical properties of both homopolymers, as well as the PLA/PBAT 75/25 blend. Notably, different processing conditions were adopted in terms of temperature (range 150–200°C) and other relevant processing parameters (moisture removal and nitrogen atmosphere). Analysis of PLA/PBAT blends indicated that intermolecular chain reactions took place under strong degradative conditions of PLA, yielding PLA/PBAT mixed chains (copolymers). Increasing amounts of copolymers resulted in improved phase dispersion and increased ductility, as SEM and mechanical tests indicated. Conversely, reduced PLA degradation with less copolymer formation, afforded higher modulus materials, owing to poorer dispersion of the soft phase (PBAT) into the PLA matrix. [Copyright &y& Elsevier]

In the perspective of producing a rigid renewable and environmentally friendly rigid packaging material, two comb-like copolymers of cellulose acetate (AC) and oligo(lactic acid) OLA, feeding different percentages of oligo(lactic acid) segments, were prepared by chemical synthesis in solvent or reactive extrusion in the melt, using a diepoxide as the coupling agent and were used as compatibilizers for poly(lactic acid)/plasticized cellulose acetate PLA/pAC blends. The blends were extruded at 230 °C or 197 °C and a similar compatibilizing behavior was observed for the different compatibilizers. The compatibilizer C1 containing 80 wt% of AC and 14 wt% of OLA resulted effective in compatibilization and it was easily obtained by reactive extrusion. Considering these results, different PLAX/pAC(100-X) compounds containing C1 as the compatibilizer were prepared by extrusion at 197 °C and tested in terms of their tensile and impact properties. Reference materials were the uncompatibilized corresponding blend (PLAX/pAC(100-X)) and the blend of PLA, at the same wt%, with C1. Significant increase in Young's modulus and tensile strength were observed in the compatibilized blends, in dependence of their morphologic features, suggesting the achievement of an improved interfacial adhesion thanks to the occurred compatibilization. [ABSTRACT FROM AUTHOR]