The goal of the current work was to create an antibacterial agent by using polycaprolactone/chitosan (PCL/CH) nanofibers loaded with Cordia myxa fruit extract (CMFE) as an antimicrobial agent for wound dressing. Several characteristics, including morphological, physicomechanical, and mechanical characteristics, surface wettability, antibacterial activity, cell viability, and in vitro drug release, were investigated. The inclusion of CMFE in PCL/CH led to increased swelling capability and maximum weight loss. The SEM images of the PCL/CH/CMFE mat showed a uniform topology free of beads and an average fiber diameter of 195.378 nm. Excellent antimicrobial activity was shown towards Escherichia coli (31.34 ± 0.42 mm), Salmonella enterica (30.27 ± 0.57 mm), Staphylococcus aureus (21.31 ± 0.17 mm), Bacillus subtilis (27.53 ± 1.53 mm), and Pseudomonas aeruginosa (22.17 ± 0.12 mm) based on the inhibition zone assay. The sample containing 5 wt% CMFE had a lower water contact angle (47 ± 3.7°), high porosity, and high swelling compared to the neat mat. The release of the 5% CMFE-loaded mat was proven to be based on anomalous non-Fickian diffusion using the Korsmeyer–Peppas model. Compared to the pure PCL membrane, the PCL-CH/CMFE membrane exhibited suitable cytocompatibility on L929 cells. In conclusion, the fabricated antimicrobial nanofibrous films demonstrated high bioavailability, with suitable properties that can be used in wound dressings. [ABSTRACT FROM AUTHOR]

In this study, biocompatible electrospun nanofiber scaffolds were produced using poly(-caprolactone (PCL)/chitosan (CS) and Nigella sativa (NS) seed extract, and their potential for biomedical applications was investigated. Scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), total porosity measurements, and water contact angle measurements were used to evaluate the electrospun nanofibrous mats. Additionally, the antibacterial activities of Escherichia coli and Staphylococcus aureus were investigated, as well as cell cytotoxicity and antioxidant activity, using MTT and DPPH assays, respectively. The obtained PCL/CS/NS nanofiber mat was observed by SEM to have a homogeneous and bead-free morphology, with average diameters of 81.19 ± 4.38 nm. Contact angle measurements showed that the wettability of the electrospun PCL/Cs fiber mats decreased with the incorporation of NS when compared to the PCL/CS nanofiber mats. Efficient antibacterial activity against S. aureus and E. coli was displayed, and an in vitro cytotoxic assay demonstrated that the normal murine fibroblast cell line (L929 cells) remained viable after 24, 48, and 72 h following direct contact with the produced electrospun fiber mats. The results suggest that the PCL/CS/NS hydrophilic structure and the densely interconnected porous design are biocompatible materials, with the potential to treat and prevent microbial wound infections. [ABSTRACT FROM AUTHOR]