We have investigated by means of high-pressure x-ray diffraction the structural stability of Pd2Mo3N, Ni2Mo3C0.52N0.48, Co3Mo3C0.62N0.38, and Fe3Mo3C. We have found that they remain stable in their ambient-pressure cubic phase at least up to 48 GPa. All of them have a bulk modulus larger than 330 GPa, being the least compressible material Fe3Mo3C, B0 = 374(3) GPa. In addition, apparently a reduction of compressibility is detected as the carbon content increased. The equation of state for each material is determined. A comparison with other refractory materials indicates that interstitial nitrides and carbides behave as ultra-incompressible materials., Comment: 14 pages, 3 figures, 1 table

We have studied by means of high-pressure x-ray diffraction the structural stability of Ni2Mo3N, Co3Mo3N, and Fe3Mo3N. We also report ab initio computing modeling of the high-pressure properties of these compounds, Pd2Mo3N, and Pt2Mo3N. We have found that the nitrides remain stable in the ambient-pressure cubic structure at least up to 50 GPa and determined their equation of state. All of them have a bulk modulus larger than 300 GPa. Single-crystal elastic constants have been calculated in order to quantify the stiffness of the investigated nitrides. We found that they should have a Vickers hardness similar to that of cubic spinel nitrides like gamma-Si3N4, Comment: 25 pages, 6 figures, 3 tables

We report on the first Raman data of Cu substituted La(1-y)Sr(y)Mn(1-x)Cu(x)O3 (0 < x < 0.10 and 0.17 < y < 0.3, accordingly in order to have the same Mn(4+)/[Mn(4+)+Mn(3+)] ratio), collected in the frequency range 100-900 cm-1 and at room temperature, with parallel and crossed polarizations of the incident and scattered light. Spectra were fitted with a Drude-Lorentz model, and peaks at 190-220 and 430 cm-1, together with two broad structures centered at near 500 and 670 cm-1, have been found. We also have observed that the A1g mode is substantially shifted with increasing Cu substitution. The A1g phonon shift is a linear function of the tolerance factor t and the rhombohedral angle, thus following the structural changes of the MnO6 octahedra in the system., Comment: 6 pages, 4 figures, SSC (accepted)