Multi‐walled carbon nanotubes (MWCNT) were first non‐covalently functioned by tannic acid (TA), then blended with nitrile rubber (NBR) and ethylene propylene diene monomer (EPDM) with NBR:EPDM:TA‐MWCNT = 70:30:5. TA‐MWCNT and the composites had been characterized by various techniques, including Fourier transform infrared spectroscopy (FT‐IR), Raman analysis, transmission electron microscopy (TEM), mechanical properties testing, thermal‐oxidative aging testing, differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), and scanning electron microscopy (SEM). Results indicated that TA molecules were successfully absorbed to the surface of MWCNT. And compared with NBR/EPDM/MWCNT composites, the compatibility between NBR and EPDM had been significantly improved. The NBR/EPDM/TA‐MWCNT exhibited excellent mechanical properties and thermal‐oxidative aging properties due to the phenolic hydroxyl groups on the surface of TA‐MWCNT, which had high chemical reactivity and physical adhesion. These phenolic hydroxyl groups gave TA‐MWCNT better dispersion in the rubber matrixes and can participate in the vulcanization process, creating the firm interface between the rubber matrixes and the surface of MWCNT. [ABSTRACT FROM AUTHOR]

In this paper, a novel method has been successfully developed to prepare the polyamide 6/polystyrene/montmorillonite (APA6/PS/MMT) blends. The X-ray diffraction analysis, differential scanning calorimetry, scanning electron microscopy analysis, contact angle measurement, water absorption measurement, thermogravimetric analysis and mechanical properties test were performed separately to study the effects of P(St-co-IEM)-MMT-MPS on crystallinity, morphology, water resistance, thermal stability and mechanical properties. The results indicate the addition of MMT can promote the formation of the γ-phase. Moreover, it can improve the interfacial compatibility, water resistance, thermal stability and toughness. [ABSTRACT FROM AUTHOR]

Polydimethylsiloxane (PDMS)‐modified Kaolin was prepared by the reaction between kaolin and PDMS. MC nylon 6/kaolin and MC nylon 6/kaolin‐PDMS composites with different filler contents were prepared through in situ polymerization. Thermogravimetric analysis and differential scanning calorimetry analysis show that the feeding of kaolin improved thermal stability and crystallinity of nylon. When 1 wt% addition of kaolin‐PDMS, the tensile strength and impact strength of the as‐prepared composites reached a maximum value of 77.7 MPa and 4.5 kJ/m2, respectively, exhibiting remarkable mechanical properties. Meanwhile, the water absorption capacity of the as‐prepared composites was greatly reduced by 60% with the addition of kaolin, and the modified kaolin possesses even better performances. The results show that the treated kaolin can greatly enhance the properties of cast nylon and has an outstanding application prospect. [ABSTRACT FROM AUTHOR]