An injectable chelate-setting hydroxyapatite cement (IP6-HAp), formed by chelate-bonding capability of inositol phosphate (IP6), was developed. The effects of ball-milling duration of starting HAp powder and IP6 concentration on the material properties such as injectability and mechanical strength of the cement were examined. The cement powder was prepared by ball-milling the as-synthesized HAp powder for 5 min using ZrO 2 beads with a diameter of 10 mm, followed by another 60 min with ZrO 2 beads with a diameter of 2 mm, and thereafter surface-modified with 5000 ppm of IP6 solution. Injectable cement was then fabricated with this HAp powder and 2.5 mass% chitosan as a mixing solution, with a setting time of 36.3 ± 4.7 min and a compressive strength of 19.0 ± 2.1 MPa. The IP6-HAp cements prepared with chitosan showed favorable biocompatibility in vitro using an osteoblast cell model, and osteoconductivity in vivo using a pig tibia model.

Autograft has been carried out for anterior cruciate ligament (ACL) reconstruction surgery. However, it has negative aspect because patients lose their healthy ligaments from other part. We focus on a chitosan-hydroxyapatite (HAp) composite fiber as a scaffold of ligament regeneration. Chitosan- HAp composite fiber was made by using coagulation method. Chitosan-NaH 2 PO 4 solution was coagulated with coagulation bath including calcium ion to get the mono-fiber and then treated with sodium hydroxide solution to form HAp in fiber matrix. The mechanical property of the fiber was improved by the stretching of the wet one because of the orientation of chitosan molecule and the interaction between chitosan and HAp. Maximum stress was improved with increasing of sodium dihydrogen phosphate until 0.03 M. The swelling ratio of the fiber was inhibited by composited with HAp. Additionally, bone-bonding ability was confirmed by SBF soaking tests. [ABSTRACT FROM AUTHOR]