Search

Biodegradable aliphatic polyesters need to be tough for commodity-plastic applications, such as disposable bags. Herein, we show that chitosan nanowhiskers (CsWs) prepared from naturally abundant chitin is an effective nanofiller that reinforces the strength and toughness of poly(butylene succinate) (PBS). In-situ polycondensation of an aqueous solution of processed CsWs led to a PBS nanocomposite with the highest tensile strength (77 MPa) and elongation at break (530%) reported to date for all PBS types at a minimal nanofiller content of 0.2 wt%. The observed 3.2-fold increase in toughness of the CsW/PBS composite compared to neat PBS is superior to those of composites prepared using cellulose nanocrystals, chitin nanowhiskers, and unstably dispersed CsWs in 1,4-butanediol monomer. Interestingly, CsWs efficiently overcome the disadvantages of the PBS film that easily tears. The highly polar surfaces of the CsWs strongly bind to polymer chains and promote a fibrillar and micro-void structure, thereby maximizing the chain-holding ability of the nanofiller, which resists external tensile and tear stress. This sustainable all-organic nanocomposite is a promising candidate for biodegradable disposable commodities., Competing Interests: Declaration of competing interest The authors declare no competing financial interest., (Copyright © 2021 Elsevier B.V. All rights reserved.)

Composite materials have been extensively studied to optimize properties such as lightness and strength, which are the advantages of plastics. We prepared a highly concentrated (30 wt %) nylon/chitosan nanowhisker (CSW) masterbatch by blending nylon 6,10 and CSW by solvent casting to achieve high dispersion efficiency while considering an industrial setting. Subsequently, 0.3 wt % nylon/CSW nanocomposites were prepared with a large quantity of nylon 6,10 via melt blending. During preparation, the materials were stirred in the presence of formic acid at different times to investigate the effect of stirring time on the structure of the CSW and the physical properties of the composite. The formation of nanocomposites by the interactions between nylon and CSW was confirmed by observing the change in hydrogen bonding using FT-IR spectroscopy and the rise in melting temperature and melting enthalpy through differential scanning calorimetry. The results demonstrated increases in complex viscosity and shear thinning. The rheological properties of the composites changed due to interactions between CSW and nylon, as indicated by the loss factor. The mechanical properties produced by the nanocomposite stirred for 1.5 h were superior, suggesting that formic acid caused minimal structural damage, thus verifying the suitability of the stirring condition. [ABSTRACT FROM AUTHOR]

The demand for face masks is increasing exponentially due to the coronavirus pandemic and issues associated with airborne particulate matter (PM). However, both conventional electrostatic‐ and nanosieve‐based mask filters are single‐use and are not degradable or recyclable, which creates serious waste problems. In addition, the former loses function under humid conditions, while the latter operates with a significant air‐pressure drop and suffers from relatively fast pore blockage. Herein, a biodegradable, moisture‐resistant, highly breathable, and high‐performance fibrous mask filter is developed. Briefly, two biodegradable microfiber and nanofiber mats are integrated into a Janus membrane filter and then coated by cationically charged chitosan nanowhiskers. This filter is as efficient as the commercial N95 filter and removes 98.3% of 2.5 µm PM. The nanofiber physically sieves fine PM and the microfiber provides a low pressure differential of 59 Pa, which is comfortable for human breathing. In contrast to the dramatic performance decline of the commercial N95 filter when exposed to moisture, this filter exhibits negligible performance loss and is therefore multi‐usable because the permanent dipoles of the chitosan adsorb ultrafine PM (e.g., nitrogen and sulfur oxides). Importantly, this filter completely decomposes within 4 weeks in composting soil. [ABSTRACT FROM AUTHOR]