Search

Casein is a naturally derived amino group (-NH2) rich protein, that enables surface functionalization leading to hydrophilicity, which in turn facilitates better cell adhesion. Casein obtained from either commercial β-casein rich skim milk (A2 milk) or dissolved air flotation (DAF) technology was tested for its potential for tissue engineering applications in a comparative study. A novel biodegradable biomaterial was synthesized from casein by chemically modifying with methacrylic anhydride (MA) and combined with polyvinyl alcohol (PVA) and polyvinyl pyrrolidone (PVP) blend. The resulting methacrylated casein (CasMA) with the two polymers was processed into porous scaffolds with low and high MA concentrations to demonstrate CasMA's ease of modification and reproducibility. Fourier Transform Infrared Microscopy (FTIR) and Proton Nuclear Magnetic Resonance (1H NMR) revealed the presence of all the components and the successful modification of casein. The rheological and morphological analysis presented viscous behaviour and columnar hollow tube-like microstructures in agreement with the biomaterials' swelling and biodegradation behaviour. The live/dead in vitro assay showed high cell viability that agreed with the cell proliferation (MTT) assay in vitro, which indicated increased proliferation upon casein modification at appropriate biomaterial concentrations and volumes. This study not only showed a possible mechanism of casein methacrylation but also presented the potential use of waste materials like DAF-casein as a value-added product for tissue engineering applications.

Elevated levels of nuclear Y-box binding protein 1 (YB-1) are linked to poor prognosis in cancer. It has been proposed that entry into the nucleus requires specific proteasomal cleavage. However, evidence for cleavage is contradictory and high YB-1 levels are prognostic regardless of cellular location. Here, using confocal microscopy and mass spectrometry, we find no evidence of specific proteolytic cleavage. Doxorubicin treatment, and the resultant G2 arrest, leads to a significant increase in the number of cells where YB-1 is not found in the cytoplasm, suggesting that its cellular localisation is variable during the cell cycle. Live cell imaging reveals that the location of YB-1 is linked to progression through the cell cycle. Primarily perinuclear during G1 and S phases, YB-1 enters the nucleus as cells transition through late G2/M and exits at the completion of mitosis. Atomistic modelling and molecular dynamics simulations show that dephosphorylation of YB-1 at serine residues 102, 165 and 176 increases the accessibility of the nuclear localisation signal (NLS). We propose that this conformational change facilitates nuclear entry during late G2/M. Thus, the phosphorylation status of YB-1 determines its cellular location. Agency for Science, Technology and Research (A*STAR) Published version We thank the Cancer Society of New Zealand (11/07), the Maurice Wilkins Centre of New Zealand and the Dean’s Bequest Fund (Dunedin School of Medicine) for their funding support of this project. We also acknowledge the Health Research Council (HRC) of New Zealand and the Royal Society James Cook Fellowship for their ongoing support of Antony Braithwaite and his lab group. The Westmead Institute of Medical Research (WIMR) Flow Cytometry Centre, supported by the Australian NHMRC and the Cancer Institute NSW are thanked for cell sorting. Anthony Cesare and his lab are supported by grants from the NHMRC (1053195, 1106241). Srinivasaraghavan Kannan and Chandra Verma would like to thank A*STAR and National Supercomputer Centre Singapore for support. Srinivasaraghavan Kannan and Chandra Verma are founders/scientific consultants of Sinopsee Therapeutics, a biotechnology company developing molecules for therapeutic purposes; the current work does not conflict with the company.

High levels of the cold shock protein Y-box-binding protein-1, YB-1, are tightly correlated with increased cell proliferation and progression. However, the precise mechanism by which YB-1 regulates proliferation is unknown. Here, we found that YB-1 depletion in several cancer cell lines and in immortalized fibroblasts resulted in cytokinesis failure and consequent multinucleation. Rescue experiments indicated that YB-1 was required for completion of cytokinesis. Using confocal imaging we found that YB-1 was essential for orchestrating the spatio-temporal distribution of the microtubules, &beta, actin and the chromosome passenger complex (CPC) to define the cleavage plane. We show that phosphorylation at six serine residues was essential for cytokinesis, of which novel sites were identified using mass spectrometry. Using atomistic modelling we show how phosphorylation at multiple sites alters YB-1 conformation, allowing it to interact with protein partners. Our results establish phosphorylated YB-1 as a critical regulator of cytokinesis, defining precisely how YB-1 regulates cell division.

A xenograft (bovine hydroxyapatite [BHA]) was developed from New Zealand sourced bovine cancellous bone by a successful defatting and deproteinizing procedure. The BHA was chemically, compositionally and structurally characterized. Fourier transform infrared spectroscopy confirmed the removal of organic matter from the bone matrix and the presence of carbonate ( CO32-), hydroxyl (OH- ), and phosphate ( PO43-) functional groups. X-ray diffraction analysis suggested that the processed bone corresponds characteristically to hydroxyapatite (HA). SEM analysis showed that the BHA has an interconnected porous architecture with a pore diameter ranging from 100 to 700 μm while µCT analysis calculated the total porosity as 73.46% ± 1.08. Furthermore, the BHA was stable up to 1000°C and lost only 1.8% of its weight. The Ca/P molar ratio of the BHA was 1.58, which is comparable with commercially available natural HA-Endobon® . After 28 days of incubation in simulated body fluid (SBF), the pH value only fluctuated between 7.1 and 7.5 and the BHA scaffold did not degrade significantly by weight indicating the scaffold had excellent chemical and structural stability. In vitro studies showed the BHA was cytocompatible and supported the proliferative growth of Saos-2 osteoblast cells. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 1054-1062, 2017.

Diclofenac potassium loaded sutures based upon PEG/PCL/chitosan-keratin blends were fabricated using the hot-melt extrusion technique. Polymer sutures were evaluated based on their physical, thermal and mechanical properties, while the drug-eluting sutures were evaluated for drug release properties. Lastly, the performance of the drug-loaded sutures in the contact with the human keratinocyte cell line HaCat were assessed. Results showed that the sutures extruded homogeneously at a temperature of 63 ± 1 °C providing a uniform thickness of fibres. Analysis by Differential Scanning Calorimetry (DSC) and Thermogravimetric Analysis (TGA) showed that completely amorphous and miscible solid dispersions were created. Fourier transform infrared (FTIR) spectroscopy indicated that the presence of hydrogen bonds between the polymers improved material miscibility. Tensile properties of the sutures were clearly affected by the PEG, chitosan and keratin additions. The optimal formulation of tensile strength was obtained when PCL/PEG/chitosan-keratin were combined at a ratio of 80/19/1 w/w. Rapid and sustained drug release rates were achieved with the PEG/PCL/chitosan/keratin blends at various combinations. The composite of PCL/PEG/chitosan-keratin with 30 wt% of diclofenac potassium also exhibited high cell viability and wound healing rates in vitro cytotoxicity testing. The anti-inflammatory properties imparted by the PCL/PEG/chitosan/keratin/drug sutures may further the use of composite sutures for wound healing in clinical settings.

A bovine dentine derived hydroxyapatite (BDHA) bone graft was developed from waste bovine teeth using a successful defatting and deproteinizing procedure. The resulting BDHA material was characterised using several analytical techniques to investigate its chemical, physical, thermal and structural properties. Fourier-transform-infrared-spectroscopy spectra confirmed the presence of carbonate, hydroxyl and phosphate functional groups which is associated with hydroxyapatite. X-ray diffraction analysis suggested that the processed BDHA corresponds characteristically to hydroxyapatite. Scanning electron microscopy showed the presence of dentinal tubules with an interconnected porous architecture in conjunction with a pore diameter of ∼3-4 μm. Thermogravimetric analysis showed that the BDHA was stable up to 1000 °C and lost only 1.5% of its weight. Both Inductively-coupled-plasma-mass spectrometry and Energy-dispersive-X-ray analysis revealed that the inorganic phases of BDHA were mainly composed of calcium and phosphorous with trace amounts of sodium and magnesium. The BDHA was chemically stable and did not degrade significantly after 28 days of incubation in simulated body fluid (SBF). The BDHA material showed excellent mechanical properties in terms of yield strength and young’s modulus. In-vitro studies showed that the BDHA was non-toxic, supported the proliferative growth of Saos-2 cells and expressed the bone marker “osteonectin” after 14 days.

Calcium phosphate ceramics that mimic bone composition provide interesting possibilities for the advancement in bone tissue engineering. The present study reports on a chitosan composite reinforced by hydroxyapatite (HA) and β-tricalcium phosphate (β-TCP) obtained from waste mussel shells and cross-linked using tripolyphosphate (TPP). The ratios of the ceramic components in composites were 20/10/70, 30/20/50 and 40/30/30 (HA/β-TCP/CH, w/w %). Biodegradation rate, structural properties and in-vitro degradation of the bone-like composite scaffolds were investigated. The optimum amount of TPP required for composite was 2.5% and glycerol was used as plasticizer at an optimized concentration of 1%. Tripolyphosphate cross-linked chitosan composites were developed by freezing and lyophilisation. The Young's modulus of the scaffolds was increased from 4kPa to 17kPa and the porosity of composites dropped from 85 to 68% by increasing the HA/β-TCP ratio. After 28days in physiological solution, bone-like composite scaffolds with a higher ratio of HA/β-TCP (e.g. 40/30/30) showed about 2% lower biodegradation in comparison to scaffolds with a lower ratio of HA/β-TCP (i.e. 20/10/70). The obtained data suggest that the chitosan based bone-like composites could be potential candidates for biomedical applications.

There are significant problems in obtaining normal human material for histology for teaching or research purposes. This study shows that tissue from cadavers embalmed for teaching can be used for routine histology. Twelve cadavers embalmed with four different formalin-containing embalming fluids were used (n = 3 per fluid): (1) formalin mix (10% formalin); (2) Dunedin mix (an alcohol-based fluid containing phenol); (3) Michigan mix (a water-based fluid); and (4) phenoxyethanol mix (an alcohol-based fluid containing phenoxyethanol). Tissue blocks of liver, heart, kidney, skin and skeletal muscle were taken from each cadaver, paraffin embedded, sectioned and stained with haematoxylin and eosin (H & E), Periodic Acid Schiff (PAS), or Mallory trichrome (Malt). Each section was assigned an overall score based on the histological quality of the cellular components of the tissue. Sections were scored from 1 to 3 (1 = poor, 2 = satisfactory, 3 = good). Satisfactory sections were obtained from all cadavers except those embalmed with the Dunedin mix. The Michigan and phenoxyethanol fluids resulted in consistently good quality sections. No significant differences in tissue morphology were observed between the different stains. The clearest morphology was observed in the skin and skeletal muscle sections, and in tissues embalmed with fluids which do not contain phenol.

Squid pen chitosan was used in the fabrication of biocomposite scaffolds for bone tissue engineering. Hydroxyapatite (HA) and beta-tricalcium phosphate (β-TCP) obtained from waste mussel shells were used as the calcium phosphate source. The composite was prepared using 2.5% tripolyphosphate (TPP) and 1% glycerol as a cross-linker and plasticizer, respectively. The weight percent (wt.%) ratios of the ceramic components in the composite were 20/10/70, 30/20/50 and 40/30/30 (HA/β-TCP/Chi). The biodegradation rate and structural properties of the scaffolds were investigated. Scanning electron microscopy (SEM) and microCT(μCT) results indicated that the composites have a well defined lamellar structure with an average pore size of 200 μm. The porosity of the composites decreased from 88 to 56% by increasing the ratio of HA/β-TCP from 30 to 70%. After 28 days of incubation in a physiological solution, the scaffolds were degraded by approximately 30%. In vitro investigations showed that the composites were cytocompatible and supported the growth of L929 and Saos-2 cells. The obtained data suggests that the squid pen chitosan composites are potential candidates for bone regeneration.