In recent years, lithium fluoride (LiF) detectors based on the optical reading of photoluminescence emitted by radiation-induced F2 and F3+ colour centres have been successfully used for advanced diagnostics of proton beams. In this work, the visible photoluminescence response of LiF film-based radiation detectors of three different thicknesses, grown by thermal evaporation on glass and Si(100) substrates and irradiated with 27 MeV proton beams at doses in the range between 4.2 × 103 and 1.7 × 105 Gy, was carefully investigated by fluorescence optical microscopy. Before irradiation, the structural and morphological properties of LiF films were investigated by atomic force microscopy and X-ray diffraction techniques. Substrate-enhanced photoluminescence response up to 48% was observed in LiF film-based detectors grown on Si(100) substrates with respect to those deposited on glass in the same deposition run and irradiated in the same conditions. This photoluminescence enhancement can be mainly ascribed to the reflective properties of the Si substrate in the visible spectral range, where the emission bands of F2 and F3+ colour centres are located, combined with the proper choice of the film thickness. Other complex effects related to the polycrystalline nature of the LiF films cannot be excluded.

In the last few years, the peculiar photoluminescence properties of radiation-induced color centers in lithium fluoride (LiF) films have been successfully used for advanced diagnostics of low-energy proton beams produced by the TOP-IMPLART linear accelerator for protontheraphy under development at ENEA C.R. Frascati. The two-dimensional spatial dose map of the transversal section of proton beams was fully reconstructed in a wide interval of doses. In this work the optical emission properties of LiF thin films, grown by thermal evaporation on glass and Si(100) substrates and subsequently irradiated by proton beams of nominal energy 3 MeV at doses higher than 105 Gy, were carefully investigated. Their structural and morphological analyses were performed by X-ray diffraction and atomic force microscopy. A careful comparison of the photoluminescence and photoluminescence-excitation spectra of F2 and F3+ electronic defects was performed. Substrate-enhanced photoluminescence intensity increase up to 100% was observed in colored LiF films grown on Si substrates with respect to glass ones. This behavior can be substantially ascribed to the reflective properties of the Si substrate at the emission wavelengths of F2 and F3+ CCs, although other complex effects due to the polycrystalline nature of the films cannot be excluded.

Colour centres (CCs) in lithium fluoride (LiF) are well known for application in tuneable lasers and dosimeters. The visible photoluminescence (PL) of radiation-induced, broad-band light-emitting aggregate CCs in LiF crystals and films has been proposed for high spatial resolution X-ray imaging; use of LiF-based detectors has been recently successfully extended to advanced diagnostics of low-energy proton beams. After exposure, transversal dose mapping was obtained on LiF films by acquiring the visible PL image of the irradiated spots in a fluorescence microscope under blue-light pumping. Irradiation of thermally evaporated LiF thin films with a proton beam of 3 MeV nominal energy, produced by a linear accelerator, in the fluence range of 1011–1015 protons/cm2, induces the formation of stable CCs, mainly the primary F centre and the aggregate F2 and F3 + defects. A comparison with irradiations performed at 7 MeV shows that the spectrally integrated PL as a function of the absorbed dose is independent on the selected beam energy, at least as far as typical LiF film thicknesses are concerned. The PL behaviour vs. dose can be described by a linear growth which covers up to three order of magnitude, followed by saturation at high values (> ≈105 Gy). The spectral contributions of F2 and F3 + CCs to the detected PL, in the red and in the green respectively, under laser pumping were carefully analysed in order to investigate behaviour differences of these defects at high doses. © 2018 Elsevier B.V.

Proton beams of 3 and 7 MeV energies, produced by a linear accelerator, were used to irradiate lithium fluoride crystals and thermally evaporated LiF thin films in the fluence range of 1011-1015 protons/cm2. The irradiation induces the formation of stable colour centres, mainly the primary F centre and the aggregate F2 and F 3 + defects. By optical pumping in the blue spectral region, the F2 and F3 + centres emit broad photoluminescence bands in the visible spectral range. By conventional fluorescence microscopy, the integrated photoluminescence intensity was carefully measured in LiF crystals and thin films as a function of the irradiation fluence: a linear optical response was obtained in a large range of fluence, which is dependent on the used LiF samples and the selected beam energy. It was possible to record the transversal proton beam intensity profile by acquiring the photoluminescence image of the irradiated spots on LiF films by a standard optical microscope. Using LiF films grown on silicon substrates irradiated in a particular geometry, the same optical reading microscopy technique allowed one to measure the distribution of colour centres photoluminescence along the depth and direct imaging the Bragg peak position, which gives a rough estimation of the initial proton beam energy.© 2014 Published by Elsevier B.V.

An Aluminum coated FBG was heated to 650 °C in order to study the regeneration process at low temperature. When compared to the standard regeneration process (at 800 °C -1000 °C) the regeneration occurred at longer times, the onset of the process took around 150 days to appear. The reflected signal after regeneration also is weaker than that obtained in the usual process, although it presents a good stability after the recovery phase - measured for a time span of 200 days. © 2015 SPIE.

LiF films grown on glass and Si(100) substrates by thermal evaporation were used as radiation imaging detectors to evaluate the Bragg peak position of a 3 MeV proton beam produced by a linear accelerator. The proton irradiation of LiF films induces the formation of stable color centers, mainly the primary F centers and the aggregate F2 and F3 + defects, whose local concentrations are proportional to the deposited energy. Under optical pumping in the blue spectral region, F2 and F3 + color centers emit broad photoluminescence bands located at 678 and 541 nm, respectively, which can be detected by conventional fluorescence microscopy. Photoluminescence images of the top surface of the exposed LiF films allowed obtaining the Bragg peak position of the proton beam, whose evaluation is in satisfactory agreement with software simulations.

Proton beams of energy 3 and 7 MeV, produced by a linear accelerator for protontherapy under development at ENEA Frascati, were used to irradiate lithium fluoride (LiF) crystals and 1 μm thick LiF films grown by thermal evaporation on glass substrates, in a fluence range from 10 11 to 10 15 protons/cm 2 . The irradiation of LiF induced the stable formation of aggregate visible-emitting F 2 and F 3 + color centers, which possess almost overlapping absorption bands around 450 nm and, under optical pumping in this spectral region, they simultaneously emit broad photoluminescence bands, peaked at 678 nm and 541 nm, respectively. Their laser excited emission spectra were acquired and the integrated photoluminescence signal was measured using a fluorescence optical microscope equipped with a cooled s-CMOS camera. The photoluminescence of proton irradiated LiF crystals and films shows an interesting linear response as a function of the irradiation fluence. By optical fluorescence microscopy, it was possible to record the transversal proton beam intensity profile by acquiring the photoluminescence image of irradiated LiF. Moreover, using cleaved LiF films grown on silicon substrates irradiated in a particular geometry allowed one to measure the colour centres photoluminescence distribution with proton penetration depth and provided a direct imaging of the Bragg peak.

Lithium fluoride is a well-known dosimeter material and it is currently under investigation also for high-resolution radiation imaging detectors based on colour centre photoluminescence. In order to extend their applications, proton beams of 3 MeV energy, produced by a linear accelerator, were used to irradiate LiF crystals and thin films in the fluence range of 1010–1015 protons/cm2. The irradiation induces the formation of colour centres, mainly the primary F centre and the aggregate F2 and F 3 + defects, which are stable at room temperature. By optical pumping in the blue spectral region, the F2 and F 3 + centres emit broad photoluminescence bands in the visible spectral range. By conventional fluorescence microscopy, the integrated photoluminescence intensity was carefully measured in LiF crystals and thin films as a function of the irradiation fluence: a linear optical response was obtained in a large range of fluence, which is dependent on the used LiF samples. Colour centres concentrations were estimated in LiF crystals by optical absorption spectroscopy. It was possible to record the transversal proton beam intensity profile by acquiring the photoluminescence image of the irradiated spots on LiF films.

Proton beams of 3 MeV energy, produced by the injector of a linear accelerator for proton therapy, were used to irradiate at room temperature lithium fluoride crystals and polycrystalline thin films grown by thermal evaporation. The irradiation fluence range was 1011-1015 protons/cm2. The proton irradiation induced the stable formation of primary and aggregate color centers. Their formation was investigated by optical absorption and photoluminescence spectroscopy. The F2 and F3 + photoluminescence intensities, carefully measured in LiF crystals and thin films, show linear behaviours up to different maximum values of the irradiation fluence, after which a quenching is observed, depending on the nature of the samples (crystals and films). The Principal Component Analysis, applied to the absorption spectra of colored crystals, allowed to clearly identify the formation of more complex aggregate defects in samples irradiated at highest fluences. © Published under licence by IOP Publishing Ltd.

Optically transparent LiF thin films thermally evaporated on glass and Si(100) substrates were used for advanced diagnostics of proton beams of energies from 1.4 to 7 MeV produced by a linear accelerator for protontheraphy under development at ENEA C.R. Frascati. The proton irradiation induces the formation of stable colour centres, among them the aggregate F2 and F3 + optically active defects. After exposure of LiF films grown on glass perpendicularly to the proton beams, their accumulated transversal spatial distributions were carefully measured by reading the latent two-dimensional (2-D) fluorescence images stored in the LiF thin layers by local formation of these broad-band visible light-emitting defects with an optical microscope under blue lamp excitation. Taking advantage from the low thickness of LiF thin films and from the linear behaviour of the integrated F2 and F3 + photoluminescence intensities up to the irradiation fluence of ∼5x1015 p/cm2, placing a cleaved LiF film grown on Si substrate with the cutted edge perpendicular to the proton beam, the 2-D fluorescence image of the film surface could allow to obtain the depth profile of the energy released by protons, which mainly lose their energy at the end of the path. © Published under licence by IOP Publishing Ltd.

In this work we tested use of thin film aluminium coating to enhance the temperature sensing features of FBG sensors. Thin film coating was evaporated on the Bragg grating after removal of the original acrylate recoating, using a modified vacuum evaporation system that allows uniform radial deposition around the fibre. Results show that recoating thickness up to 0.5 μm do not produce appreciable effects, whereas thickness of 2.3 μm appreciably increases temperature sensitivity without increasing time response constant. © 2013 SPIE.

Systematic irradiation of thermally evaporated 0.8 μm thick polycrystalline lithium fluoride films on glass was performed by proton beams of 3 and 7 MeV energies, produced by a linear accelerator, in a fluence range from 1011to1015protonscm2. The visible photoluminescence spectra of radiation-induced F2 and F3+laser active color centers, which possess almost overlapping absorption bands at about 450 nm, were measured under laser pumping at 458 nm. On the basis of simulations of the linear energy transfer with proton penetration depth in LiF, it was possible to obtain the behavior of the measured integrated photoluminescence intensity of proton irradiated LiF films as a function of the deposited dose. The photoluminescence signal is linearly dependent on the deposited dose in the interval from 103 to about 106Gy, independently from the used proton energies. This behavior is very encouraging for the development of advanced solid state radiation detectors based on optically transparent LiF thin films for proton beam diagnostics and two-dimensional dose mapping. © 2015 AIP Publishing LLC.