Seven laboratories participated in an interlaboratory study to assess the applicability of ASTM E606, Test Method for Strain-Controlled Fatigue Testing, to strain-controlled fatigue of a tungsten fiber/copper matrix composite (Battelle Columbus, University of Iowa, IITRI, MCL, MarTest, Rockwell International Science Center and University of Twente). Because of the material and specimen fabrication methods, the number of fibers in the 9, 25, and 36 % fiber volume fraction specimens is approximately the same and the strain-life data are nearly identical for each of the volume fractions. Although the specimen aspect ratio is within the nominal range, the specimen diameter is less than the nominal value specified in ASTM E606. Laboratories reporting data noted that a small specimen diameter and a large gage section aspect ratio made specimen alignment difficult. Thus, specimen buckling was problematic at high strain ranges. The study data are reported and analyzed with nonparametric and semiparametric statistical methods to assess the effect of study covariates on fatigue life. The median fatigue life, median absolute deviation from the median, and interquartile range are reported as measures of central tendency and variability. ASTM E606 may be used as a guide to evaluate the fatigue response of this type of composite material if the length-to-diameter aspect ratio, specimen alignment in the fatigue machine, and specimen surface finish are closely monitored to ensure valid data.

Substantial improvements have been reported in high temperature strength and creep resistance, and room temperature fracture toughness of molybdenum disilicide (MoSi2) reinforced with ductile or brittle reinforcements. The influence of Hot Isostatic Pressing (HIP) process parameters on the mechanical properties of MoSi2 based alloys was studied. Monolithic MoSi2 powder and MoSi2 powder blended with either niobium powder or silicon carbide whisker reinforcements were consolidated by HIP at 1200 − 1400°C, 207 MPa, and 1 - 4 hrs. The HIP'ed compacts were characterized for compression strength and creep resistance at 1100-1300°C. Fracture toughness was measured on single edge notched rectangular specimens at room temperature. Mechanical properties were correlated with post-HIP microstructural features.