Copyright of La Revista Latinoamericana de Metalurgia y Materiales, RLMM is the property of Universidad Simon Bolivar, Departmento de Ciencia de los Materiales and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Cerium-doped MoO3 thin films were grown through spray pyrolysis using (NH4) 6Mo7O 24 4H2O 0.1 M solution. The doping was performed by adding 0.1M CeCl3.7H2O, in a ratio of 2% by volume. X-ray and Auger electron spectra show of Ce incorporation in MoO3 thin film. X-ray diffraction showed that Cerium insertion destroys the α-MoO3 structure observed in undoped films. The electrochemical properties were studied using the cyclic voltammetry technique with -400 to 400 mV and scanning speeds from 16 to 144 mV/s. It was established that the diffusion coefficient varies from 1.06 x 10-10 cm²/s for the undoped film to 3.49 x 10 cm²/s for doped film. This suggests that the doped film favors ion exchange processes. The optical transmittance in the range of 290-2500 nm showed that the light transmission of the film doped with Cerium is higher by 10% compared to the undoped film. [ABSTRACT FROM AUTHOR]