Search

The market share of zirconia (ZrO2) dental implants is steadily increasing. This material comprises a polymorphous character with three temperature-dependent crystalline structures, namely monoclinic (m), tetragonal (t) and cubic (c) phases. Special attention is given to the tetragonal phase when maintained in a metastable state at room temperature. Metastable tetragonal grains allow for the beneficial phenomenon of Phase Transformation Toughening (PTT), resulting in a high fracture resistance, but may lead to an undesired surface transformation to the monoclinic phase in a humid environment (low-temperature degradation, LTD, often referred to as ‘ageing’). Today, the clinical safety of zirconia dental implants by means of long-term stability is being addressed by two international ISO standards. These standards impose different experimental setups concerning the dynamic fatigue resistance of the final product (ISO 14801) or the ageing behavior of a standardized sample (ISO 13356) separately. However, when evaluating zirconia dental implants pre-clinically, oral environmental conditions should be simulated to the extent possible by combining a hydrothermal treatment and dynamic fatigue. For failure analysis, phase transformation might be quantified by non-destructive techniques, such as X-Ray Diffraction (XRD) or Raman spectroscopy, whereas Scanning Electron Microscopy (SEM) of cross-sections or Focused Ion Beam (FIB) sections might be used for visualization of the monoclinic layer growth in depth. Finally, a minimum load should be defined for static loading to fracture. The purpose of this communication is to contribute to the current discussion on how to optimize the aforementioned standards in order to guarantee clinical safety for the patients.

OBJECTIVES: To evaluate two-body wear of three zirconia ceramics stabilized with 3, 4 and 5mol% yttria and to compare their wear behavior with that of a lithium-disilicate glass-ceramic. METHODS: Sixteen rectangular-shaped specimens made from three grades of zirconia ceramics and a lithium-disilicate glass-ceramic were polished and dynamically loaded in a chewing simulator (2kg vertical load, 2.1Hz) under water at 90°C for 1.2×106 cycles (about 7 days) in the ball-on-plate mode against steatite antagonists. Surface roughness was measured before and after wear testing. Wear tracks were scanned with a non-contact 3D profilometer and super-impositions were used to determine wear loss of the antagonists. Wear surfaces were imaged by SEM. XRD and micro-Raman spectroscopy were used to characterize phase transformation and stress status in the worn and unworn areas of the zirconia ceramics. RESULTS: Independent of fracture toughness, strength and aging-susceptibility, the three zirconia ceramics showed a similar and limited amount of wear (∼10μm in depth) and were more wear-resistant than the lithium-disilicate glass-ceramic (∼880μm in depth). Abrasive wear without obvious cracks was observed for all investigated zirconias, whereas the glass-ceramic with a lower fatigue threshold and high susceptibility to surface dissolution exhibited significant abrasion, fatigue and corrosion wear. All three zirconia ceramics yielded a lower antagonist wear than the glass-ceramic and no significant differences were found between the zirconia ceramics. SIGNIFICANCE: In the context of this study, high-translucent zirconia ceramics stabilized with a higher yttria content, recently introduced in the dental field, were as wear-resistant and antagonist-friendly as conventional high-strength zirconia and suitable for monolithic restorations. ispartof: DENTAL MATERIALS vol:35 issue:12 pages:1776-1790 ispartof: location:England status: published

OBJECTIVES: For the use of partially stabilized zirconia (PSZ) as high-translucent zirconia, the importance of cubic phase (c-ZrO2) is commonly emphasized without much attention for the remaining tetragonal phase (t-ZrO2). The aim is to understand whether the crystal structure and microstructure of t-ZrO2 have paramount influences on the properties of PSZ. METHODS: Two grades of 5mol% yttria-stabilized PSZ ceramics were prepared by different processing routes. A 5mol % yttria co-precipitated zirconia (T5Y) was compared with a 3 and 8mol% yttria-stabilized powder mixture grade with a bimodal grain size distribution (B5Y). The phase composition and lattice parameters were studied with x-ray diffraction (XRD) and Rietveld analysis. Mechanical properties were compared in terms of hardness, toughness and biaxial bending strength with Weibull analysis. Their translucency and aging stability were also characterized, and the microstructure before and after aging were followed by scanning electron microscopy (SEM). RESULTS: T5Y and B5Y having similar phase composition (about 40% t- and 60% c-ZrO2) showed the same basic properties (density, hardness and toughness), but the lattice parameters of t-ZrO2 and the concomitant microstructure were completely different. The t-ZrO2 phase in T5Y had a higher yttria content and a lower tetragonality (c/a) of 1.0126±0.0002, whereas the t-ZrO2 phase in B5Y was comparable to that in conventional 3Y-TZPs with a tetragonality of 1.0153±0.0002. Consequently, B5Y showed a lower strength with lower Weibull modulus, being less translucent and more aging susceptible as compared to T5Y. The translucency and aging susceptibility of B5Y were even comparable to those of conventional 3Y-TZP. SIGNIFICANCE: Not only the phase composition with high cubic phase content but also the lattice parameters and the yttria content in the remaining t-ZrO2 played a determinant role for PSZs to be used as 'high-translucent' zirconia. ispartof: DENTAL MATERIALS vol:36 issue:4 pages:491-500 ispartof: location:England status: published

Made available in DSpace on 2020-12-12T02:24:49Z (GMT). No. of bitstreams: 0 Previous issue date: 2020-09-01 Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) Fundação de Amparo à Pesquisa do Estado do Rio de Janeiro (FAPERJ) Objectives: The aim of this study was to evaluate the effect of hydrothermal aging on the mechanical properties and translucency of dental zirconia with different levels of translucency. Methods: Three different types of dental yttria-stabilized zirconia were used: 3Y-TZP (ZrO2 - 3 mol.% Y2O3) of medium opacity (designated Z3OP), 3Y-TZP of medium translucency (Z3MT), and 5Y-PSZ (ZrO2 - 5 mol.% Y2O3) of high translucency (Z5HT). A total of 120 specimens were sintered (n = 40 specimens/group). The control group (sintered→polished→heat-treated) and the aged group (sintered→polished→heat-treated→hydrothermally degraded at 134 °C, 2 bar, 5h) were characterized by relative density, quantitative phase analysis by X-ray diffraction using the Rietveld method, microstructural analysis by scanning electron microscopy, surface roughness and translucency. All groups were submitted to a biaxial flexural strength test. Data analysis using Kruskal-Wallis, Nemenyi (p-value = 0.05), and Weibull statistics were used. Results: All sintered specimens presented full densification. After aging, an increase of the m-ZrO2 phase content was observed for the Z3OP group. On the other hand, Z3MT and Z5HT did not show any m-ZrO2 phase, indicating resistance to the hydrothermal degradation. Smaller grains were observed in the Z3MT group in relation to Z3OP group and the Z5HT group presented a bimodal grain distribution, where the largest grains were associated to cubic ZrO2. Z3OP exhibited a slight increase in roughness as a function of degradation, while the roughness remained statistically stable in the other groups. Translucency was little influenced by degradation, but considerably affected by increasing thickness. The Z5HT samples were the group with the highest translucency among the control groups. Z3OP exhibited the highest flexural strength, while being the most susceptible to hydrothermal degradation. The lowest values were presented by Z5HT in all groups, due to the high concentration of c-ZrO2 grains. Conclusion: Hydrothermal aging is less critical to the flexural strength of zirconia-based materials than the materials’ composition and microstructure. Z5HT zirconia showed the highest translucency, however the measured difference is not visually perceptible. Z5HT was considered the most resistant to hydrothermal degradation. Fluminense Federal University Faculty of Dentistry Institute of Health of Nova Friburgo, Dr. Silvio Henrique Braune St, 22 - Downtown Pontical Catholic University of Rio de Janeiro Department of Chemical and Materials Engineering PUC-Rio, Marques de São Vicente St 225, Gávea University of Toronto Faculty of Dentistry, 124 Edward St #539 State University of Rio de Janeiro Faculty of Technology, Presidente Dutra Highway, Km 298 São Paulo State University Faculty of Engineering of Guaratinguetá UNESP/FEG, Ariberto Pereira da Cunha Ave, 333 - Portal Das Colinas São Paulo State University Faculty of Engineering of Guaratinguetá UNESP/FEG, Ariberto Pereira da Cunha Ave, 333 - Portal Das Colinas CNPq: 308684/2013-3/311119/2017-4 FAPERJ: E-26-201.476/2014

cited By 3; International audience; Objectives: The dental market moves towards high-translucency monolithic zirconia dental crowns, which are usually placed either with – or without – a thin glaze layer. The microstructural features and the mechanical performances of these materials are still controversial, as well as their susceptibility to aging. This paper aims at studying these aspects in the current generation of zirconia dental crowns showing different degrees of translucency. Methods: Four different commercial zirconia materials were investigated, including one standard ‘full-strength’ 3Y-TZP and three grades with improved translucency. The microstructural features (phase composition and assemblage, grain size) were carefully studied, as well as mechanical properties (biaxial bending strength and indentation toughness), translucency and aging behavior (in autoclave at 134 °C). Aging was conducted on crowns with and without glaze to better represent clinical uses. Results: Important differences are found in terms of microstructures among the materials in terms of cubic phase content and yttria in the tetragonal phase, leading to different optical, mechanical and aging resistance properties. We show that higher cubic phase content leads to better translucency and stability in water steam, but at the expense of strength and toughness. A compromise is always inevitable between translucency and aging resistance on one side and mechanical properties on the other side. Significance: - Even so called ‘high translucent’ zirconia ceramics tested in this work should be considered as medium translucency materials.- Aging occurs in standard state-of-the-art dental zirconia and glazing does not fully avoid this issue. However, aging did not compromise strength even after prolonged duration.- Aging is null in the ‘highly translucent’ zirconia grades but at the expense of strength, which is then comparable to glass-ceramics. © 2018 The Academy of Dental Materials

Made available in DSpace on 2019-09-12T16:53:37Z (GMT). No. of bitstreams: 0 Previous issue date: 2016 Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) NUFFIC (Netherlands Organization for International Cooperation in Higher Education, The Netherlands) agency (Grants CAPES/NUFFIC) [056/14] The following study aimed to evaluate the effect of grinding and low-temperature aging on the fatigue limit of Y-TZP ceramics for frameworks and monolithic restorations. Disc specimens from each ceramic material, Lava Frame (3M ESPE) and Zirlux FC (Ivoclar Vivadent) were manufactured according to ISO:6872-2008 and assigned in accordance with two factors: (1) "surface treatment"-without treatment (as-sintered, Ctrl), grinding with coarse diamond bur (181 mu m; Grinding); and (2) "low-temperature aging (LTD)" - presence and absence. Grinding was performed using a contra-angle handpiece under constant water-cooling. LTD was simulated in an autoclave at 134 degrees C under 2-bar pressure for 20 h. Mean flexural fatigue limits (20,000 cycles) were determined under sinusoidal loading using stair case approach. For Lava ceramic, it was observed a statistical increase after grinding procedure and different behavior after LTD stimuli (Ctrl