Abstract: A series of TiO2–SiO2 mixtures – having the following stoichiometry Ti1−x Si x O2, with x =0, 0.1, 0.3 and 0.5 atoms per formula unit – were prepared by using precursor oxides and fired at three temperatures (900, 1000 and 1200°C). The modifications in the structure and, consequently, on the photocatalytic activity, induced by the addition of SiO2 into the TiO2 powder, were thoroughly investigated by using various analytical techniques: X-ray powder diffraction, electron microscopy (FE-SEM and TEM), XPS, FT-IR, DRS and BET analysis. The results underlined as essentially no solid solution occurs between the two crystalline end-members. Nevertheless, silica addition caused a retarding effect on anatase-to-rutile phase transformation and on the crystallite growth. The photocatalytic activity of the powders was assessed in gas phase and the results were explained by taking into account the anatase and rutile relative amounts in the samples, their crystallite size, the surface hydroxyl groups adsorbed on the photocatalysts and the surface area of the mixtures. [Copyright &y& Elsevier]

The use of wastes, some of them hazards, as raw materials of ceramic pigments has been a way to diminish their environmental impact, to economically valorize them, and to face the depletion of virgin raw materials. In this work were prepared pigments having in their composition only industrial wastes: Cr/Ni electroplating (ES), and sludges from the cutting of natural stones—marble (MS) and granite (GS). The prepared mixtures were calcined at three temperatures (1100, 1200, and 1300 °C) and the obtained powders were characterized by XRD and UV-vis. Their coloring strength and thermal stability were assessed by adding them to different ceramic substrates: glazes (transparent bright and opaque matte) and a stoneware paste. The CIEL*a*b* coordinates of the fired materials were measured. The developed pigments are thermally stable and exhibit good tinting power, originating nicely colored and defect-free ceramic materials. [ABSTRACT FROM AUTHOR]