Search

PTFE coatings were deposited on YT15 carbide substrates using spray technology. A series of examinations were conducted, including the use of surface and cross-section micrographs to analyze the structural integrity of the coatings. The surface roughness, the adhesion force between the PTFE coatings and the carbide substrate, and the micro-hardness of the coated carbide were also evaluated. Additionally, the friction and wear behaviors were assessed through dry sliding friction tests against WC/Co balls. The test results indicated that while the PTFE-coated carbide exhibited a rougher surface and reduced micro-hardness, it also demonstrated a significant reduction in surface friction and adhesive wear. These findings suggest that the PTFE coatings enhance the overall wear resistance of the carbides. The lower surface hardness and shear strength of the coatings influenced the friction performance, leading to specific wear failure mechanisms, such as abrasion wear, coating delamination, and flaking. Overall, the deposition of PTFE coatings on carbide substrates presents a promising strategy to enhance their friction and wear performance. This approach not only improves the durability of carbide materials but also offers potential applications in industries where reduced friction and wear are critical for performance. [ABSTRACT FROM AUTHOR]

To improve the surface friction characteristics of cemented carbide, a Cr coating was deposited on cemented carbide substrate with the multiple arc plating technique. The surface and cross-section micrographs, adhesion force and micro-hardness of the Cr-coated cemented carbide were tested. The anti-friction and anti-wear behaviors of cemented carbide with and without Cr coating were investigated via the sliding friction test against a WC/Co ball. The tribological properties of cemented carbide were examined using a scanning electron microscope and energy dispersive X-ray analysis. The test results showed that Cr-coated cemented carbide possessed good adhesion properties and lower hardness. The average coefficient of friction for Cr-coated cemented carbide was reduced by 10–20% compared with that of an uncoated one. The primary wear modes of the Cr-coated sample were delamination of coating, flaking and abrasion wear. It can be found that the preparation of a Cr coating is an effective way to enhance the friction and wear performance of traditional cemented carbide. [ABSTRACT FROM AUTHOR]

To expand the industrial application of cemented carbide, micro-EDM was utilized to machine microhole-textures on the carbide surface; graphite powder was burnished into the textured microholes. The tribological properties of the microhole-textured tool combined with graphite were investigated and compared with the conventional one by carrying out reciprocating sliding friction tests and dry machining tests. Results exhibited that the microhole-textured tool combined with graphite possessed a much lower friction coefficient than that of the conventional one in sliding tests. The cutting forces, average friction coefficient at the tool–chip interface, and rake face wear of the textured tool were reduced, and the workpiece surface quality was also slightly improved. The worn regions of carbide specimen were examined and studied, and the possible effect mechanisms for the enhancement of friction and wear properties mainly consisted of the formation of uneven graphite film by friction extrusion, reduction of actual contact length, entrapment of wear debris and supply of graphite lubricant. [ABSTRACT FROM AUTHOR]

In order to enhance the tribological performance of YT14 carbide, pure Zr coating was deposited on the substrate surface using a multi-arc ion plating method. The surface topography, adhesion strength, thickness, and micro-hardness of the Zr coating were tested. Dry sliding friction experiments against a 40Cr hardened steel ring were conducted with Zr-coated carbides and traditional ones. The average coefficients of friction were measured and compared. The wear characteristics of the samples were examined by scanning electron microscope (SEM) and energy dispersive X-ray analysis (EDX). The test results indicated that the Zr coating deposited on the carbide surface exhibited excellent adhesive strength and lower hardness. The average friction coefficient of Zr coated carbide decreased by 20%–30% in comparison with that of the uncoated one. The Zr coated carbide could reduce the adhesive wear compared with the uncoated one, and the main tribological degradation mechanisms of the coating were abrasive wear, coating flaking and delamination. [ABSTRACT FROM AUTHOR]