Exposure to elevated temperatures has detrimental effects on the properties of cementitious composites, leading to irreversible changes, up to total failure. Various methods have been used to suppress the deterioration of concrete under elevated temperature conditions. Recently, nanomaterials have been introduced as admixtures, which decrease the thermal degradation of cement-based composites after exposure to high temperatures. This paper presents a comprehensive review of recent developments related to the effects of nanoparticles on the thermal resistance of cementitious composites. The review provides an updated report on the effects of temperature on the properties of cement-based composites, as well as a detailed analysis of the available literature regarding the inclusion of nanomaterials and their effects on the thermal degradation of cementitious composites. The data from the studies reviewed indicate that the inclusion of nanoparticles in composites protects from strength loss, as well as contributing to a decrease in disruptive cracking, after thermal exposure. From all the nanomaterials presented, nanosilica has been studied the most extensively. However, there are other nanomaterials, such as carbon nanotubes, graphene oxide, nanoclays, nanoalumina or nano-iron oxides, that can be used to produce heat-resistant cementitious composites. Based on the data available, it can be concluded that the effects of nanomaterials have not been fully explored and that further investigations are required, so as to successfully utilize them in the production of heat-resistant cementitious composites. [ABSTRACT FROM AUTHOR]

This study presents the results of an experimental investigation of the effects of nanosilica (NS) on the strength development, transport properties, thermal conductivity, air-void, and pore characteristics of lightweight aggregate concrete (LWAC), with an oven-dry density <1000 kg/m3. Four types of concrete mixtures, containing 0 wt.%, 1 wt.%, 2 wt.%, and 4 wt.% of NS were prepared. The development of flexural and compressive strengths was determined for up to 90 days of curing. In addition, transport properties and microstructural properties were determined, with the use of RapidAir, mercury intrusion porosimetry (MIP), and scanning electron microscopy (SEM) techniques. The experimental results showed that NS has remarkable effects on the mechanical and transport properties of LWACs, even in small dosages. A significant improvement in strength and a reduction of transport properties, in specimens with an increased NS content, was observed. However, the positive effects of NS were more pronounced when a higher amount was incorporated into the mixtures (>1 wt.%). NS contributed to compaction of the LWAC matrix and a modification of the air-void system, by increasing the amount of solid content and refining the fine pore structure, which translated to a noticeable improvement in mechanical and transport properties. On the other hand, NS decreased the consistency, while increasing the viscosity of the fresh mixture. An increment of superplasticizer (SP), along with a decrement of stabilizer (ST) dosages, are thus required. [ABSTRACT FROM AUTHOR]