The design of cathodic catalysts layer (CCL) consisted of Platinum Group Metal-free (PGM-free) electrocatalysts was done by catalyst coated membrane approach. Three different Fe-Mn-N-C compounds were synthesized with Fe:Mn ratio of 1:1, 2:1 and 2:1 with modified heat treatment profile. The catalysts were characterized by X-ray photoelectron spectroscopy, X-ray powder diffraction, pore and particle size distribution, zeta potential and transmission electron microscopy. Electrocatalysts were integrated into membrane electrode assembly and evaluated by electrochemical methods. Electrochemical impedance spectroscopy in combination with modeling were used for estimation of proton conductivity of CCL and its oxygen diffusivity. It was found that all CCLs possess extremely high proton conductivity, which was demonstrated for the first time for these types of PGM-free catalysts. The observed ORR mechanism was predominantly 4e- due to peroxide/radicals scavenging effect of Mn. [Display omitted] • Bi-metallic Fe-Mn-N-C PGM-free catalysts were synthesized. • Highly performed, industrial quality MEAs were fabricated. • Detailed electrochemical fuel cell evaluation was combined with EIS modeling. • The proton conductivity in catalyst layer was improved 5 times vs literature data. [ABSTRACT FROM AUTHOR]

To elucidate the evolution of ionomer-Pt and ionomer-carbon interfaces during life cycle of polymer electrolyte fuel cells (PEFCs), electrodes with high surface area (HSA) and durable carbon supports underwent catalyst and carbon corrosion accelerated stress tests (ASTs) under stoichiometric and sub-stoichiometric gas flow conditions. Electrochemical characterizations, as well as X-ray photoelectron spectroscopy (XPS) were utilized to assess degree of components degradation. Catalyst AST results revealed that Pt nanoparticles dispersed within the micro- and meso-pores and not in contact with ionomer are the main contributor to the 50% electrochemical surface area (ECSA) loss observed after 30k cycles resulting in significant polarization loss, which is much more notable in the case of sub-stoichiometric operating condition. Support AST results for HSA carbon showed severe ionomer degradation and 55% ECSA loss within the first 100 cycles, while cell with durable support exhibited negligible polarization and ECSA decay during the first 2500 cycles attributed to higher ionomer coverage, preservation of proton pathways preventing Pt from detachment. [Display omitted] • Interfaces evolution are evaluated during accelerated stress tests (ASTs) for fuel cells. • Pt that is not in contact with ionomer degrades the most for catalyst AST. • Ionomer degradation is observed for all ASTs. • Graphitized carbon supports mitigate corrosion and Pt loss. [ABSTRACT FROM AUTHOR]