Search

Carbon nanotube (CNT)‐polyetherimide (PEI) hybrid nanofibrous veils were prepared through the electrospinning process to function as an interlayer in carbon fiber reinforced polymer composites (CFRP), and the effects of the addition of the hybrid fiber veils on the interlaminar fracture properties and flexural properties of CFRP were investigated. The results showed that interleaving CNT/PEI hybrid veils can effectively avoid long‐troubled trade‐off between mode‐I interlaminar fracture toughness and in‐plane properties when using thermoplastic toughening materials. Specifically, the GIc value and flexural strength of the laminates were increased by as much as 86.2% and 14.3%, respectively when CNT content was reached up to 0.7 wt% in CNT/PEI hybrid veil. This method adopts ultra‐low PEI and CNT additions, and the limited quantity of these additives demonstrates a notably high interlaminar toughening efficiency while concurrently enhancing the strength, rendering it a promising strategy for both toughening and strengthening. Highlights: PEI is used as a carrier to transport CNT to the CFRP interlaminar layers.PEI‐CNT hybrid fiber veils improve GIC and flexural strength of CFRP.PEI‐CNT hybrid fiber veils impede crack expansion through various mechanisms.This method adopts ultra‐low PEI and CNT additions. [ABSTRACT FROM AUTHOR]

In this study, aramid fiber (AF)/phenolic resin prepreg was fabricated by impregnating low content carbon nanotube (CNT)‐reinforced phenolic resin with aramid fabric through a two‐roll pressing process. Both non‐functionalized and carboxylic‐functionalized CNTs (CNTs and CNTs‐COOH) were used for comparison study. For each of the formulations, composite laminate was made by a hot‐pressing process with a number of the prepregs stacked together. Mechanical properties and ballistic performance of the laminates and material failure mechanisms were evaluated and analyzed. Both non‐functionalized and CNTs‐COOH can effectively improve the mechanical and ballistic performance of the laminates. With CNTs‐COOH reinforcement, better results were achieved. As compared with the laminate without CNT reinforcement, 1.0 wt% CNTs‐COOH‐reinforced laminate showed 19.41%, 22.29%, and 45.83% improvement in tensile, flexural, and adhesion shear strength, respectively. The ballistic test results showed that the V50 and the specific energy absorption (SEA) were increased by 5.77% and 13.44%, respectively. The correlation between mechanical and ballistic performance of the composites was analyzed and conducted. [ABSTRACT FROM AUTHOR]

"Interleaving" is widely used for interlaminar toughening of fiber-reinforced composites, and the structure of interleaving is one of the important factors affecting the toughening efficiency of laminates. Several experiments have demonstrated that compared to continuous and dense structures, toughening layers with structural heterogeneity can trigger multiple toughening mechanisms and have better toughening effects. On this basis, this work further investigates the application of heterogeneous toughening phases in interlaminar toughening of bidirectional GFRP. CNT was selected to construct toughening phases, which was introduced into the interlaminar of composites through efficient spraying methods. By controlling the amount of CNT, various structures of CNT toughening layers were obtained. The fracture toughness of modified laminates was tested, and their toughening mechanism was analyzed based on fracture surface observation. The results indicate that the optimal CNT usage (0.5 gsm) can increase the initial and extended values of interlayer fracture toughness by 136.0% and 82.0%, respectively. The solvent acetone sprayed with CNT can dissolve and re-precipitate a portion of the sizing agent on the surface of the fibers, which improves the bonding of the fibers to the resin. More importantly, larger discrete particles are formed between the layers, guiding the cracks to deflect in the orientation of the toughened layer. This generates additional energy dissipation and ultimately presents an optimal toughening effect. [ABSTRACT FROM AUTHOR]

Carbon fiber reinforced polymer composites have the advantages of being lightweight, having high strength and designability, and having been extensively used. However, the interlaminar toughness and delamination resistance of these composites are relatively poor due to their laminated structure and intrinsic brittleness of resin matrix. In this paper, commercialized free-standing carbon nanotube (CNT) films, drawn from CNT forests, were used to toughen the interlaminar interfaces of the composites. The effects of resin infiltration state and thickness of CNT films on the interlaminar toughening effect were systematically investigated. The results show that the pre-infiltration treatment of CNT films with acetone diluted epoxy resin solution can effectively improve the degree of resin infiltration. Compared with the samples containing untreated CNT film, the Mode I and Mode II interlaminar fracture toughness of the treated samples were significantly improved. The GIC reached a maximum of 1412.42 J/m2 at a CNT film thickness of 5 µm, which was about 61.38% higher than that of the baseline. At a CNT film thickness of 15 µm, the GIIC reached a maximum value of 983.73 J/m2, approximately 67.58% higher than that of the baseline. The corresponding toughening mechanisms were also systematically analyzed. [ABSTRACT FROM AUTHOR]

• BFRP bars was treated by CNTs modified resin to improve the corrosion resistance in alkaline concrete environment. • The mechanical properties of untreated and treated BFRP bars with CNTs modified resin were evaluated after 180 d immersion. • The microcosmic deterioration mechanism of untreated and treated BFRP bars with modified resin CNTs were investigated using Micro-CT, FTIR, TG and SEM. The corrosion of basalt fiber-reinforced polymer (BFRP) bars restricts their use in alkaline concrete structures. However, developing high-performance resin can improve the anti-alkaline corrosion of BFRP bars. This work investigates the alkaline resistance of BFRP bars by coating carbon nanotubes (CNTs) modified epoxy resin incorporating varying CNTs contents (0, 0.1, 0.3, and 0.5 wt%). The durability of untreated and treated BFRP bars with CNT-modified resin was evaluated using water uptake, transverse shear, and interlaminar shear tests. Scanning electron microscopy (SEM) and X-ray micro-computed tomography (micro-CT) were also used to observe the surface corrosion morphology and interior deterioration of BFRP bars, respectively, while Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA) were applied to analyze the resin deterioration of BFRP bars. It was found that CNTs modified resin can significantly improve the alkaline resistance of BFRP bars. After 180 d of immersion, the interlaminar shear strength (ILSS) retention of untreated BFRP bars is 31.8%, while it is 63.3, 75.0, 91.3, and 93.7% for BFRP bars treated with 0, 0.1, 0.3, and 0.5 wt% CNTs modified resin, respectively. The improvements in ILSS retention of BFRP bars treated with 0.5 wt% CNTs modified resin are 61.9% and 30.4% more than untreated and pure resin-treated BFRP bars, respectively. BFRP bars treated with 0.3 and 0.5 wt% CNTs modified resin exhibit insignificant resin hydrolysis and less porosity than untreated BFRP bars. The effective prevention of hydroxyl ions into the interior of BFRP bars and the enhancement of the anti-crack behavior of resin by CNTs are the leading causes of corrosion resistance improvement in BFRP bars. The outcomes of this study provide insights into using CNTs modified resin to improve the durability of BFRP bars in marine concrete structures. [ABSTRACT FROM AUTHOR]

Ultrathin CNT fiber veils (100–300 nm thick) were used as interleaves to improve the interlaminar fracture toughness of unidirectional carbon fiber reinforced polymer composites. These veils, drawn from vertically aligned CNT forests, were directly deposited at the mid-plane of CFRPs either longitudinally or transversely to the carbon fiber. The results revealed that triggering multiple toughening mechanisms is the key to achieve high toughness FRP composites. When the veils were oriented parallelly to the carbon fiber, the crack propagates in a "zig-zag" manner, not only interacting with more CNTs, but also triggering more carbon fiber bridgings, leading to a steeply "rising" R-curve. The superiority and effectiveness of this technique is exemplified by the extremely thin toughening layers (about 300 nm thick) needed to remarkably improve the propagation value of Mode I interlaminar fracture toughness of the CFRP by approximately 107%. The Mode I toughening factor (η I), defined as the change in Mode I interlaminar fracture toughness per interleaf-to-ply thickness ratio, comes out as high as 713, which is far outweigh the state-of-the-art. However, transversely-placed CNT veils will seriously block the formation of carbon fiber bridgings, remarkably degrading the Mode I interlaminar toughness of the laminates. [Display omitted] [ABSTRACT FROM AUTHOR]