Search

A composite filler was developed by pre-flocculation of fiber fines and precipitated calcium carbonate (PCC) particles with flocculants such as cationic polyacrylamide (cPAM) and bentonite. The composite filler was compared with a conventional loading method in terms of physical properties of handsheet and filler retention. The handsheets using the composite filler showed higher strength properties than that using a conventional loading at a similar paper ash content level, implying that paper ash content can be increased maintaining same level of paper strength. Optical properties such as opacity and brightness of the paper with the composite were quite similar with the paper with the conventional loading. Filler retention of the composite filler was slightly higher than that of the conventional loading even though retention aids were not used for the composite filler. Paper formation of the composite filler was better than the case of the conventional loading. However, the sheet with the composite filler showed lower bulk than that with the conventional loading. Conclusively, the composite filler technology by pre-flocculation of fines and filler has a potential to be utilized to produce a high loaded paper. [ABSTRACT FROM AUTHOR]

The purpose of this study was to evaluate the feasibility of using highly filled powders with 100 parts per weight of calcium carbonate and 10 parts per weight of polymer, acting as binder, as electrostatically applied paper coatings. Such powders prepared by different methods were evaluated as being suitable for electrostatic coating. Powders compacted at elevated temperatures demonstrated cohesion superior to that of calcium carbonate, and at best similar to that of aqueous coatings. Cohesion, porosity and thus absorption properties of compacted powders were affected by the powder preparation method, compaction process, and powder composition. Powders containing semicrystalline polymer turned out to be the most interesting for further testing. [ABSTRACT FROM AUTHOR]

Precipitated calcium carbonate (PCC) is a filler that is widely used for papermaking, and lime sludge is a special type of PCC recovered from the black liquor from kraft pulping. There has been some concern that lime sludge may interfere with the development of paper's hydrophobicity in comparison with commercial PCC and ground calcium carbonate (GCC) due to the presence of impurities when alkyl ketene dimer (AKD) is used as the sizing additive. In this work, fillers with different particle size distributions were prepared, and the effects of particle composition on surface chemistry of fillers, adsorption for AKD, sizing degree of final paper sheets, and retention behavior of fillers were evaluated. The results showed that, through matching different particle size distributions for lime sludge fillers, the negative zeta potential decreased from -26.2 mV to -20.8 mV, the specific surface area decreased from 15.0 m²/g to 9.1 m²/g, and total pore volume decreased from 0.037 cm³/g to 0.026 cm³/g, which was favorable for the low adsorption for AKD. Consequently the sizing effect of filled paper was improved. Moreover, the retention rate also was increased by changing the particle size distribution of lime sludge. [ABSTRACT FROM AUTHOR]

Inorganic fillers are inexpensive materials used to increase the density, smoothness and other properties of paper that are important for printing. In the current study, the adhesion of pressure-sensitive adhesives (PSAs), a common type of adhesive used in labels and tapes, to papers containing varying amounts and types of fillers is investigated. Papers with three types of fillers, precipitated calcium carbonate (PCC), ground calcium carbonate (GCC) and kaolin clay, were investigated. The compositions of the papers were examined with SEM/EDX, while peel and double cantilever beam (DCB) tests were used to assess PSA-paper adhesion. The results indicate that fillers enhance the adhesion between PSA and paper. In the case of the peel tests, a combination of inter-fiber bond strength and PSA-paper adhesion determines the peel strength. While in the DCB tests, failure is isolated to the PSA-paper interface, thus allowing measurements of pure interfacial failure. [ABSTRACT FROM AUTHOR]