Abstract: To improve the oxidation resistance of carbon/carbon (C/C) composites, a C/SiC/MoSi2–Si multilayer oxidation protective coating was prepared by slurry and pack cementation. The microstructure of the as-prepared coating was characterized by scanning electron microscopy, X-ray diffraction and energy dispersive spectroscopy. The isothermal oxidation and erosion resistance of the coating was investigated in electrical furnace and high temperature wind tunnel. The results showed that the multilayer coating could effectively protect C/C composites from oxidation in air for 300h at 1773K and 103h at 1873K, and the coated samples was fractured after erosion for 27h at 1873Kh in wind tunnel. The weight loss of the coated specimens was considered to be caused by the formation of penetration cracks in the coating. The fracture of the coated C/C composites might result from the excessive local stress in the coating. [Copyright &y& Elsevier]

Abstract: To protect carbon/carbon (C/C) composites against oxidation, a Si–Mo coating was prepared on C/SiC-coated C/C composites by a simple slurry method. The microstructure of the coating was characterized by X-ray diffraction, scanning electron microscopy and Raman spectra. Results showed that the coating was mainly composed of SiC, MoSi2 and Si. It could protect C/C composites from oxidation at 1873K in air for 300h and withstand 13 thermal cycles between room temperature and 1873K. The excellent oxidation and thermal shock resistance of the coating was attributed to the formation of dense SiO2 glass at high temperature. The volatilization of MoO3 and SiO2 at 1873K was the main reason of the weight loss of the coated C/C composites. [Copyright &y& Elsevier]

Abstract: To protect carbon/carbon (C/C) composites against oxidation, a SiC nanowire-toughened MoSi2–SiC coating was prepared on them using a two-step technique of chemical vapor deposition and pack cementation. SiC nanowires obtained by chemical vapor deposition were distributed random-orientedly on C/C substrates and MoSi2–SiC was filled in the holes of SiC nanowire layer to form a dense coating. After introduction of SiC nanowires, the size of the cracks in MoSi2–SiC coating decreased from 18±2.3 to 6±1.7μm, and the weight loss of the coated C/C samples decreased from 4.53% to 1.78% after oxidation in air at 1500°C for 110h. [Copyright &y& Elsevier]