Search

We investigate the surface morphologies of two series of homoepitaxial GaSb(100) thin films grown on GaSb(100) substrates by molecular beam epitaxy in a Veeco GENxplor system. The first series was grown at temperatures ranging from 290 to 490 ° C and serves as a control. The second series was grown using the same growth parameters with bismuth used as a surfactant during growth. We compared the two series to examine the impacts of bismuth over the range of growth temperatures on the GaSb surface morphologies using atomic force microscopy and the film properties using Raman spectroscopy and scanning electron microscopy. High-resolution x-ray diffraction was performed to confirm that bismuth was not incorporated into the films. We found that the morphological evolution of the GaSb series grown without bismuth is consistent with the standard surface nucleation theory and identified the 2D-3D transition temperature as close to 290 ° C. In contrast, the presence of a Bi surfactant during growth was found to significantly alter the surface morphology and prevent undesired 3D islands at low temperatures. We also observed a preference for hillocks over step morphology at high growth temperatures, antistep bunching effects at intermediate temperatures, and the evolution from step-meandering to mound morphologies at low temperatures. This morphological divergence from the first series indicates that bismuth significantly increases in the 2D Erlich–Schwöebel potential barrier of the atomic terraces, inducing an uphill adatom flux that can smoothen the surface. Our findings demonstrate that bismuth surfactant can improve the surface morphology and film structure of low-temperature grown GaSb. Bismuth surfactant may also improve other homoepitaxial III-V systems grown in nonideal conditions. [ABSTRACT FROM AUTHOR]

Films of n-GaAs1-xBix films were grown via molecular beam epitaxy using both Si and Te as dopant sources. Electron mobility was characterized by Hall effect measurements as a function of carrier concentration and Bi content for films with bismuth fractions of x = 0.02 and x = 0.06. While GaAsBi:Te shows lower majority carrier mobility than GaAsBi:Si at low Bi concentrations, the two become comparable as Bi content increases. Furthermore, it was observed that in the presence of bi-metallic Bi-Ga droplets on the film surface, films doped with Si display p-type behavior, likely due to Si preferentially occupying group-V sites. The use of Te as a dopant always resulted in n-type epilayers, making it a more reliable dopant choice for high Bi content films. Finally, ex situ annealing was studied as a method to improve majority carrier mobility in GaAs0.98Bi0.02:Te films, with a 10 min anneal at 350 °C resulting in a 30% improvement in electron mobility. Improvement of film quality was confirmed through spectroscopic ellipsometry examination of film optical properties. Annealing at higher temperatures resulted in electrical, optical, and structural degradation of the GaAsBi films. [ABSTRACT FROM AUTHOR]

GaAs1−xBix has been grown by solid-source molecular beam epitaxy using varying substrate rotation rates. Changes in local bismuth saturation were studied by varying the Bi/Ga pressure ratio across the wafer. Films were grown on both GaAs and InGaAs buffer layers with varying indium content to change the strain conditions of the bismide layer and the out-of-plane growth rate. All samples demonstrated vertical composition modulations with a period of ∼ 4 nm that tracked with the rate of growth per substrate rotation cycle. The thermal stability of these composition modulations was shown to behave similarly to bulk GaAsBi. Bismide composition modulations are attributed to the low growth temperature and the varying Bi/Ga pressure ratio across the sample rather than the varying V/III ratio. [ABSTRACT FROM AUTHOR]