Search

In recent years, natural polymer‐based electrospun fibers (EFs) with huge specific surface area, good biocompatibility, and biological activity obtained from electrospinning process exhibit tremendous vitality in the field of biomedical areas. Herein, the parameters of electrospinning from two perspectives, polymer solution such as solvent, polymeric relative molecular mass, concentration, viscosity, and conductivity of the solution, and electrospinning process such as spinning voltage, spinning flow rate, needle tip to collector distance, temperature, and humidity are first detailed. Next, the raw materials consisting of polysaccharides such as cellulose, hyaluronic acid, alginate, and chitosan as well as proteins such as collagen, gelatin, silk fibroin, and keratin are summarized. The preparation method and related characteristics of EFs with multistage structures such as porous, core–shell, Janus, bamboo‐like and other structures are introduced. The biomedical applications of these natural polymer‐based EFs mainly including tissue engineering, drug sustained release, wound dressings, and biomedical sensors are systematically recapitulated. Finally, the outlook on natural EFs is further proposed. [ABSTRACT FROM AUTHOR]

ABSTRACT Cotton stalk bark fibers (CSBF) were prepared using combined steam explosion and laccase treatment (explosion-laccase). CSBF have been applied to reinforce thermoplastic composites, but were difficult to be spun into yarns due to their inferior fineness and high stiffness. In order to improve the fineness and flexibility with a green method, explosion-laccase treatment was used to separate bark of cotton stalks. The results indicated that steam explosion at 1.7 MPa for 3 min effectively facilitated laccase penetration into the lignocellulose complex to enhance delignification without negative effects on activity of laccase. Compared with CSBF after explosion, CSBF after explosion-laccase had better fineness (31 dtex), higher aspect ratio (1110), higher tensile strength (2.81 cN/dtex), higher flexibility (321 twist/(m·dtex)), and better thermal stability, which meets the requirement of textile fibers. CSBF had higher water retention (127%) and moisture regain (10.3%) than cotton. Explosion-laccase is an effective and eco-friendly method of preparing CSBF for textiles. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017, 134, 45058. [ABSTRACT FROM AUTHOR]

ABSTRACT Keratin particles with microscale are prepared by ball mill and its influences on the chitosan membrane is evaluated. Composite membranes with various content of keratin are fabricated, and their physical and chemical properties such as morphology, wettability, crystallization, thermal stability, tensile strength, and break elongation are investigated. Optical microscope and situ topographic scan mode of nano-test system are used to examine the dispersion and aggregation of keratin on the surface of chitosan membrane. The result of contact angle (CA) and mechanical testing show that the incorporation of keratin particles decrease the CA from 98.1° to 58.2°. Tensile strength and break elongation of the composite membrane reaches a maximum of 65 ± 8 MPa and 15% when the keratin content is 6%, an increase of 80% and 88% compared with the pristine chitosan membrane. Both the increase in tensile strength and break elongation is result of the incorporation of keratin particles known for their excellent compatibility between keratin and chitosan matrix. These kind of composite material combines the antibacterial properties of chitosan with cell culture preference of keratin which may have potential biomedical application. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017, 134, 44667. [ABSTRACT FROM AUTHOR]

The article discusses a study on the preparation and characterization of cellulose/chitin blend filaments obtained from cellulose/chitin xanthalate blend solution over an experimental blend ratio. The study showed that chitin xanthalate addition into cellulose xanthalate resulted in an increase of intermittence rate. It also concluded that the degree of crystallinity, density and accessibility of blend filaments decreases with increasing chitin content.

A clean and cost-effective method for 100% stereo-complexation in polylactide (PLA) fibers with molecular weight (MW) as high as 6 × 10 5 demonstrates good potential for industrial-scale continuous manufacture. Polylactide, a widely recognized biodegradable and renewable biopolymer, has a negligible share of plastic markets due to its poor hydrolytic and thermal resistance. Stereo-complexation is effective in overcoming these challenges. However, current stereo-complexation approaches usually require solvents and/or external nucleation reagents, and are expensive and complicated. Moreover, high-MW PLAs favored for developing durable products are difficult to be stereo-complexed. In this research, enantiomeric PLAs both with MW up to 6 × 10 5 were completely stereo-complexed via a facile thermal treatment on pilot-scale devices. Neither solvent nor nucleation agent was used. For poly(L-lactide) (PLLA) fibers with MW of 6 × 10 5 , percentage retention of MW and percentage retention of tensile strength after hydrolysis under simulated textile dyeing condition increased from 39% to 93% and from 20% to 89%, respectively, after complete stereo-complexation. The melting point, softening point and percentage retention of MW after hydrolysis of stereo-complexed PLA (sc-PLA) fibers were up to 51 °C, up to 59 °C and up to 183% higher than that of PLLA fibers with the same MW, respectively. The mechanism of thorough stereo-complexation in high-MW PLA fibers was proposed and verified. It is promising to use this approach to broaden industrial applications of renewable and degradable biopolymers for sustainable development of material industries. [ABSTRACT FROM AUTHOR]