Search

Biowastes from agriculture, sewage, household wastes, and industries comprise promising resources to produce biomaterials while reducing adverse environmental effects. This study focused on utilising waste-derived materials (i.e., eggshells as a calcium source, struvite as a phosphate source, and CH3COOH as dissolution media) to produce value-added products (i.e., calcium phosphates (CaPs) derived from biomaterials) using a continuous flow hydrothermal synthesis route. The prepared materials were characterised via XRD, FEG-SEM, EDX, FTIR, and TEM analysis. Magnesium whitlockite (Mg-WH) and hydroxyapatite (HA) were produced by single-phase or biphasic CaPs by reacting struvite with either calcium nitrate tetrahydrate or an eggshell solution at 200 °C and 350 °C. Rhombohedral-shaped Mg-WH (23–720 nm) along with tube (50–290 nm diameter, 20–71 nm thickness) and/or ellipsoidal morphologies of HA (273–522 nm width) were observed at 350 °C using HNO3 or CH3COOH to prepare the eggshell and struvite solutions, and NH4OH was used as the pH buffer. The Ca/P (atomic%) ratios obtained ranged between 1.3 and 1.7, indicating the formation of Mg-WH and HA. This study showed that eggshells and struvite usage, along with CH3COOH, are promising resources as potential sustainable precursors and dissolution media, respectively, to produce CaPs with varying morphologies. [ABSTRACT FROM AUTHOR]

Varying formulations in the glass system of 40P2O5─(24 − x)MgO─(16 + x)CaO─(20 − y)Na2O─yTiO2 (where 0 ≤ x ≤ 22 and y = 0 or 1) were prepared via melt‐quenching. The structure of the glasses was confirmed by X‐ray diffraction (XRD), Fourier transform infrared (FTIR), micro Raman and solid‐state nuclear magnetic resonance (NMR) spectroscopies. The thermal properties and the activation energy of crystallization (Ec) were measured using thermal analysis and the Kissinger equation, respectively. The glass forming ability of the formulations investigated was seen to decrease with reducing MgO content down to 8 mol% and the glass stability region also decreased from 106 to 90°C with decreasing MgO content. The activation energy of crystallization (Ec) values also decreased from 248 (for 24 mol% MgO glass) to 229 kJ/mol (for the 8 mol% MgO content) with the replacement of MgO by CaO for glasses with no TiO2. The formulations containing less than 8 mol% MgO without TiO2 showed a strong tendency toward crystallization. However, the addition of 1 mol% TiO2 in place of Na2O for these glasses with less than 8 mol% MgO content, inhibited their crystallization tendency. Glasses containing 8 mol% MgO with 1 mol% TiO2 revealed a 12°C higher glass transition temperature, a 14°C increase in glass stability against crystallization and a 38 kJ/mol increase in Ec in comparison to their non TiO2 containing counterpart. NMR spectroscopy revealed that all of the formulations contained almost equal percentages of Q1 and Q2 species. However, FTIR and Raman spectroscopies showed that the local structure of the glasses had been altered with addition of 1 mol% TiO2, which acted as a network modifier, impeding crystallization by increasing the cross‐linking between phosphate chains and consequently leading to increased Ec as well as their glass forming ability. [ABSTRACT FROM AUTHOR]

Phosphate-based glasses (PBGs) offer significant therapeutic potential due to their bioactivity, controllable compositions, and degradation rates. Several PBGs have already demonstrated their ability to support direct cell growth and in vivo cytocompatibility for bone repair applications. This study investigated development of PBG formulations with pyro- and orthophosphate species within the glass system (40 − x)P2O5·(16 + x)CaO·20Na2O·24MgO (x = 0, 5, 10 mol%) and their effect on stem cell adhesion properties. Substitution of phosphate for calcium revealed a gradual transition within the glass structure from Q2 to Q0 phosphate species. Human mesenchymal stem cells were cultured directly onto discs made from three PBG compositions. Analysis of cells seeded onto the discs revealed that PBG with higher concentration of pyro- and orthophosphate content (61% Q1 and 39% Q0) supported a 4.3-fold increase in adhered cells compared to glasses with metaphosphate connectivity (49% Q2 and 51% Q1). This study highlights that tuning the composition of PBGs to possess pyro- and orthophosphate species only, enables the possibility to control cell adhesion performance. PBGs with superior cell adhesion profiles represent ideal candidates for biomedical applications, where cell recruitment and support for tissue ingrowth are of critical importance for orthopaedic interventions. [ABSTRACT FROM AUTHOR]