Search

New functional materials for engineering gingival tissue are still in the early stages of development. Materials for such applications must maintain volume and have advantageous mechanical and biological characteristics for tissue regeneration, to be an alternative to autografts, which are the current benchmark of care. In this work, methacrylated gelatin (GelMa) was photocrosslinked with synthetic immunomodulatory methacrylated divinyl urethanes and defined monomers to generate composite scaffolds. Using a factorial design, with the synthetic monomers of a degradable polar/hydrophobic/ionic polyurethane (D-PHI) and GelMa, composite materials were electrospun with polycarbonate urethane (PCNU) and light-cured in-flight. The materials had significantly different relative hydrophilicities, with unique biodegradation profiles associated with specific formulations, thereby providing good guidance to achieving desired mechanical characteristics and scaffold resorption for gingival tissue regeneration. In accelerated esterase/collagenase degradation models, the new materials exhibited an initial rapid weight loss followed by a more gradual rate of degradation. The degradation profile allowed for the early infiltration of human adipose-derived stromal/stem cells, while still enabling the graft's structural integrity to be maintained. In conclusion, the materials provide a promising candidate platform for the regeneration of oral soft tissues, addressing the requirement of viable tissue infiltration while maintaining volume and mechanical integrity. There is a need for the development of more functional and efficacious materials for the treatment of gingival recession. To address significant limitations in current material formulations, we sought to investigate the development of methacrylated gelatin (GelMa) and oligo-urethane/methacrylate monomer composite materials. A factorial design was used to electrospin four new formulations containing four to five monomers. Synthetic immunomodulatory monomers were crosslinked with GelMa and electrospun with a polycarbonate urethane resulting in unique mechanical properties, and resorption rates which align with the original design criteria for gingival tissue engineering. The materials may have applications in tissue engineering and can be readily manufactured. The findings of this work may help better direct the efforts of tissue engineering and material manufacturing. [Display omitted] [ABSTRACT FROM AUTHOR]

Background: A noninvasive method to track implanted biomaterials is desirable for real‐time monitoring of material interactions with host tissues and assessment of efficacy and safety. Purpose: To explore quantitative in vivo tracking of polyurethane implants using a manganese porphyrin (MnP) contrast agent containing a covalent binding site for pairing to polymers. Study Type: Prospective, longitudinal. Animal Model: Rodent model of dorsal subcutaneous implants (10 female Sprague Dawley rats). Field Strength/Sequence: A 3‐T; two‐dimensional (2D) T1‐weighted spin‐echo (SE), T2‐weighted turbo SE, three‐dimensional (3D) spoiled gradient‐echo T1 mapping with variable flip angles. Assessment: A new MnP‐vinyl contrast agent to covalently label polyurethane hydrogels was synthesized and chemically characterized. Stability of binding was assessed in vitro. MRI was performed in vitro on unlabeled hydrogels and hydrogels labeled at different concentrations, and in vivo on rats with unlabeled and labeled hydrogels implanted dorsally. In vivo MRI was performed at 1, 3, 5, and 7 weeks postimplantation. Implants were easily identified on T1‐weighted SE, and fluid accumulation from inflammation was distinguished on T2‐weighted turbo SE. Implants were segmented on contiguous T1‐weighted SPGR slices using a threshold of 1.8 times the background muscle signal intensity; implant volume and mean T1 values were then calculated at each timepoint. Histopathology was performed on implants in the same plane as MRI and compared to imaging results. Statistical Tests: Unpaired t‐tests and one‐way analysis of variance (ANOVA) were used for comparisons. A P value <0.05 was considered to be statistically significant. Results: Hydrogel labeling with MnP resulted in a significant T1 reduction in vitro (T1 = 517 ± 36 msec vs. 879 ± 147 msec unlabeled). Mean T1 values of labeled implants in rats increased significantly by 23% over time, from 1 to 7 weeks postimplantation (651 ± 49 msec to 801 ± 72 msec), indicating decreasing implant density. Data Conclusion: Polymer‐binding MnP enables in vivo tracking of vinyl‐group coupling polymers. Evidence Level: 1. Technical Efficacy: Stage 1. [ABSTRACT FROM AUTHOR]