The biocompatibility of three sol–gel bioactive glasses with SiO2 as the main constituent (75, 72.5 and 70 mol%), identical CaO content (25 mol%), and without or with P2O5 as third constituent (0, 2.5 and 5 mol%), have been analyzed (S75, S72.5P2.5, and S70P5 glasses). These studies were performed on both untreated glasses and on glasses coated with a hydroxycarbonate apatite (HCA) layer formed in vitro by soaking 7 d in an acellular simulated body fluid. Cell attachment, spreading and proliferation were studied using neonatal rat calvaria osteoblasts. Cells attach to the three untreated glasses but show a higher efficiency on that with the higher phosphate content (S70P5). The formation of the HCA layer significantly enhances this process (1.7-fold). In all cases, attachment is followed by cell spreading on the surface of the materials, adopting the cells a flattened morphology and showing diverse anchoring cell projections. Mitotic activity has been detected on osteoblasts growing on the sol–gel glasses, being this process 2–4-fold higher when the apatite-like layer is already formed. Taking into account the results herein presented, these bioactive glasses can be considered biocompatible. In addition, their biocompatibility is greatly enhanced after induction of the formation of an HCA layer. [Copyright &y& Elsevier]

Abstract: Parathyroid hormone-related protein (PTHrP) is an important regulator of bone formation and remodeling. Our recent findings demonstrate that PTHrP (107–111) (osteostatin) loaded onto silica-based ordered mesoporous SBA15 materials exhibit osteogenic features in osteoblastic cell cultures. We aimed here to elucidate whether these peptide-coated materials might be suitable for promoting bone repair following a cavitary defect in the rabbit femur. Histological examination revealed the absence of significant inflammation or bone resorption within the time of study (4 and 8 weeks) after implantation. At 8 weeks, the peptide-unloaded materials were still separated from the bone marrow by a fibrous cap, which was greatly diminished by the presence of the PTHrP peptide. By using μCT analysis, new bone formation was evident at different distances from the implants, mainly for the latter peptide-loaded biomaterials. This was confirmed by performing immunostaining for different osteoblast markers. Our findings demonstrate that these PTHrP (107–111)-loaded bioceramics significantly improve local bone induction, as compared to that observed with the unloaded material. [ABSTRACT FROM AUTHOR]