Search

In the present study, friction stir processing (FSP) was carried out on as-cast Mg-Zn-Dy alloy to tailor grain size and texture which alter the mechanical properties and corrosion behaviour. The grain size of the as-cast alloy was reduced from 60 ± 2 µm to 3 ± 0.1 µm after FSP due to dynamic recrystallization. The effect of grain size, crystallographic orientation and fine precipitates on mechanical properties were investigated using field emission scanning electron microscope (FESEM) and electron back scattered diffraction (EBSD). The ultimate tensile strength, yield strength, % elongation and hardness of FSPed alloy improved by 55%, 60%, 53% and 46% when compared to as-cast alloy. The FSPed Mg-Zn-Dy alloy exhibited a 79% decrease in corrosion rate when compared to as-cast alloy which can be attributed to grain refinement, uniform distribution of secondary precipitates and strong basal texture. The surface of FSPed sample after immersion corrosion exhibited calcium phosphate rich minerals which help in apatite formation on the sample surface. Cytotoxicity studies using MTT assay revealed more than 80% cell viability for both as-cast and FSPed alloy illustrating non-toxic nature of both the samples. The results of this study indicate that FSPed Mg-Zn-Dy alloy is a potential material for biodegradable implants due to its high strength, corrosion resistance and biocompatibility. [ABSTRACT FROM AUTHOR]

This work evaluates the effects of laser surface modification on Mg–Zn–Gd–Nd alloy which is a potential biodegradable material for temporary bone implant applications. The laser surface melted (LSM) samples were investigated for microstructure, wettability, surface hardness and in vitro degradation. The microstructural study was carried out using scanning and transmission electron microscopes (SEM, TEM) and the phases present were analyzed using X-ray diffraction. The in vitro degradation behaviour was assessed in hank's balanced salt solution (HBSS) by immersion corrosion technique and the effect of LSM process parameters on the wettability was analyzed through contact angle measurements. The microstructural examination showed remarkable grain refinement as well as uniform redistribution of intermetallic phases throughout the matrix after LSM. These microstructural changes increased the hardness of LSM samples with an increase in energy density. The wetting behaviour of processed samples showed hydrophilic nature when processed at lower (12.5 and 17.5 J/mm2) and intermediate energy density (22.5 and 25 J/mm2), which can potentially improve cell-materials interaction. The corrosion rate of as cast Mg–Zn–Gd–Nd alloy decreased by ~83% due to LSM. [ABSTRACT FROM AUTHOR]

Abstract In order to improve the performance of magnesium (Mg) for resorbable implant applications, Mg-1Zn-2Dy alloy was developed and the surface of the alloy has been modified by melting using lasers. Laser melted samples, at different laser energy density, were then subjected to microstructural, hardness, wettability and in-vitro degradation assessment. The microstructure of the Mg-Zn-Dy alloy mainly consisted of α-Mg and eutectic phase (Mg 8 ZnDy). The melted region of the alloy surface evolved with fine grain microstructure at the near surface region and columnar grains near to the liquid solid substrate. The degree of grain size refinement obtained at the melted zone in the order of 1–2 μm. The cross sectional microhardness of the modified zone was measured by Vickers microhardness tester. Due to these microstructural refinements and solid solution strengthening the surface hardness of laser treated alloy increased by two-fold. It was found that as the energy density increased the surface roughness along with the surface energy also increased. The wetting behaviour of the surface was estimated through measuring the contact angle by dropping the polar and non-polar liquid. Results showed that the surface energy is also found to change with LSM due to changes in the surface morphology, microstructure and chemical composition of the material. The detailed degradation study was carried out by immersing the samples in hanks balances salt solution (HBSS).The improvement in the degradation behaviour followed by laser surface melting is related to the microstructural refinement as a result of rapid heating and cooling of the melted zone. Graphical abstract Unlabelled Image Highlights • Mg-Zn-Dy alloy surface was modified by laser surface melting. • Microstructural refinement and improved hardness were observed in the laser surface melted region. • Improved wettability in laser surface melting is attributed to the changes in the surface roughness and grain size. • A significant improvement in degradation rate was achieved in the laser surface melted alloy. [ABSTRACT FROM AUTHOR]

Magnesium based alloys are well-known materials for temporary implant applications. However, failures due to early degradation and bacterial infection are limiting their applications. To overcome these problems, in the present work a Mg-Zn-Dy alloy based composite surface was prepared using coating and friction stir processing (FSP) techniques. Herein, hydroxyapatite (HA) and silver (Ag) particles were deposited on Mg-Zn-Dy alloy to obtain HA and Ag coated surface (C-HAg). Later, FSP was carried out on the C-HAg surface to develop a Mg-Zn-Dy alloy based composite surface (F-HAg). Field emission scanning electron microscope (FESEM) and energy dispersive X-ray analysis (EDS) confirm the mixing of HA and Ag particles with the Mg-Zn-Dy substrate. Antibacterial studies reveal that both C-HAg and F-HAg samples inhibit Escherichia coli and Staphylococcus aureus bacteria. In vitro cytotoxicity study indicates that the both samples are non-toxic in nature. Results of in vitro corrosion study reveal a significant reduction (72%) in corrosion rate of F-HAg sample when compared to C-HAg sample. The F-HAg samples showed simultaneous improvement in corrosion resistance and antibacterial properties with good biocompatibility. The results of this study indicate that the developed composite surface is a promising material for antibacterial and biodegradable implant applications. • Surface modification of Mg-Zn-Dy alloy using coating and FSP techniques • The addition of Ag particles suppressed E. Coli and S. aureus bacterial strains • In-vitro cell culture study using MC3T3-E1 cells demonstrated good biocompatibility for both coated and composite surfaces • FSP significantly improved corrosion resistance of composite surface when compared to coated surface [ABSTRACT FROM AUTHOR]