A core-shell structure Au-based catalysts mSiO2/Au/Co3O4 HS were successfully derived from in-situ growth ZIF-67 hollow spheres, which were synthesized by a one-step soft template method. The samples were characterized by SEM, TEM, EDX, XPS, XRD and BET to confirm its successful preparation and structural features. The catalytic performance of the catalysts were evaluated by liquid phase oxidation of benzyl alcohol to benzaldehyde with O2 as the oxidant under alkaline conditions. The experimental results illustrated that reaction conditions, including effect of catalyst amount, oxygen flow rate, reaction temperature and reaction time, were optimized to be 40 mg, 50 ml/min, 140 °C and 5 h, respectively. Meanwhile, 55% conversion of benzyl alcohol and 84% selectivitiy to benzaldehyde together with the excellent reusability and stability were achieved under optimal reaction conditions, which was attributed to the core-shell structure leading to the encapsulation of Au NPs and provision of multiple active reaction interface. Based on the intermediates formed from the de-protonation of substrate, a plausible oxidation reaction mechanism with mSiO2/Au/Co3O4 HS catalysts was tentatively proposed to study the relationship between structure and catalytic performance.

As one of the ideal catalysts, noble metal materials can realize the conversion from benzyl alcohol to benzaldehyde. However, in previous reports, the loss of surface noble metal is one of the important reasons for the decrease in reaction performance. Here, a simple method was reported for stepwise fabrication of SiO 2 @Co 3 O 4 /Au@m-SiO 2 catalysts with core–shell structure. On the one hand, the core–shell structure provided abundant reaction sites for the oxidation of benzyl alcohol to benzaldehyde. On the other hand, the outer layer of m-SiO 2 effectively prevents the loss of Au nanoparticles. In this process, we studied the effects of multiple factors on the target reaction by controlling a single variable. The experimental results show that under the optimal conditions (the catalyst dosage, reaction temperature, reaction time and O 2 flow rate are 40 mg, 160 °C, 6 h, 60 ml/min, respectively), the conversion rate of the target reaction reaches 58% and the selectivity is as high as 82%. In the end, a mechanism was put forward to illustrate the underlying reaction pathway in benzyl alcohol oxidation.