Search

Life extension of light water reactors requires robust models to predict the embrittlement of reactor pressure vessel (RPV) steels under long-term neutron irradiation. Embrittlement is due to nanoscale precipitation hardening by phases containing Cu, Mn, Ni, and Si, resulting in increases of the ductile to brittle transition temperature. Embrittlement data for low flux, high fluence extended life conditions, up to 80 years or more, are largely not available. Thus, higher flux, accelerated test reactor irradiations have been used to help develop models to predict low flux embrittlement at high fluence. Here flux, or dose rate, is expressed in units of displacements per atom per second (dpa/s). The dose rate can significantly influence precipitate evolution in a way that depends on fluence (dpa), temperature, and alloy composition, as well as flux itself. Here, we explore precipitation in surveillance steels with varying compositions at high fluxes (10−5–10−6 dpa/s) produced using 70 MeV Fe2+ ion irradiations. Atom probe tomography was used to characterize the dose dependence of precipitation at very high ion irradiation dose rates, and to evaluate corresponding similarities or differences compared to neutron irradiated steels at a much lower dose rate of ≈ 5 × 10−9 dpa/s. The data show that, on average, the ion irradiation precipitate volume fractions increase by factors of ∼ 1.5 to 2 between 0.3 dpa and 1.2 dpa. Limited data show that the major effect of neutron versus ion irradiation is the former has lower precipitate number densities and larger sizes. Otherwise, the precipitates are remarkably similar in composition and volume fraction. [ABSTRACT FROM AUTHOR]

The behavior of solute atoms in an undersaturated Fe-3.3 at.%Ni model alloy upon heavy and light particle irradiations was investigated by Atom Probe Tomography. Whereas first irradiations, performed using 27 MeV Fe ions at 400 °C, highlight significant Ni enrichment on point defect clusters, solute-rich features detected after 2.8 MeV H + ion (400 °C) and 1 MeV electron (320 °C) irradiations are only associated with pre-existent microstructural defects. Nanoindentation tests show no hardening in light particle irradiated samples, strongly suggesting that no dislocation loop formed. These observations put forward the importance of point defect clusters resulting from displacement cascades in Ni clusters' formation. Image, graphical abstract [ABSTRACT FROM AUTHOR]

Nuclear reactor lifetimes may be limited by nano-scale Cu-Mn-Ni-Si precipitates (CRPs and MNSPs) that form under neutron irradiation (NI) of pressure vessel (RPV) steels, resulting in hardening and ductile to brittle transition temperature increases (embrittlement). Physical models of embrittlement must be based on characterization of precipitation as a function of the combination of metallurgical and irradiation variables. Here we focus on rapid and convenient charged particle irradiations (CPI) to both: a) compare to precipitates formed in NI; and, b) use CPI to efficiently explore precipitation in steels with a very wide range of compositions. Atom probe tomography (APT) comparisons show NI and CPI for similar bulk steel solute contents yield nearly the same precipitate compositions, albeit with some differences in their number density, size and volume fraction (f) dose (dpa) dependence. However, the overall precipitate evolutions are very similar. Advanced high Ni (>3 wt%) RPV steels, with superior unirradiated properties, were also investigated at high CPI dpa. For typical Mn contents, MNSPs have Ni 16 Mn 6 Si 7 or Ni 3 Mn 2 Si phase type compositions, with f values that are close to the equilibrium phase separated values. However, in steels with very low Mn and high Ni, Ni 2-3 Si silicide phase type precipitate compositions are observed; and when Ni is low, the precipitate compositions are close to the MnSi phase field. Low Mn significantly reduces, but does not eliminate, precipitation in high Ni steels. A comparison of dispersed barrier model predictions with measured hardening data suggests that the Ni-Si dominated precipitates are weaker dislocation obstacles than the G phase type MNSPs. • Nuclear reactor life times are limited by nano precipitates formed under irradiation. • Ion irradiations provide a rapid & affordable way to gain insight into precipitation. • Atom Probe data estimates hardening and embrittlement at lower service dose. • Advanced high Ni steels, with superior unirradiated properties, were investigated. • Simple thermodynamic models are able to predict volume fraction for alloys. [ABSTRACT FROM AUTHOR]