The astaxanthin nanocapsules (ASX-LNC) was prepared by high-pressure homogenization technology, the microstructure, stability, antioxidant activity, and in vitro release characteristics of ASX-LNC were characterized and evaluated. The ASX-LNC comprised a core material and wall materials. The core material was composed of astaxanthin oil, and the wall materials were composed of β-cyclodextrin, decapolyglycerol monooleate, soybean lecithin (PC60), glycerol, and deionized water. The mean particle size of the ASX-LNC was 206.9 ± 2.8 nm, and the polydispersity index (PdI) value was 0.218 ± 0.026. The zeta potential of ASX-LNC was −26.16 ± 0.87 mV. The loading amount of ASX-LNC was 0.546%±0.032%, and the encapsulation efficiency was 99.65%±0.13%, indicating that the preparation process was feasible. The stability of ASX-LNC was determined under different conditions, indicating good stability of the ASX-LNC. In antioxidant research, the inhibition rate of free radicals of ASX-LNC was 91.03 ± 0.87% under 250 μg/mL for 30 min, and the inhibition rate of free radicals of astaxanthin ethanol solution was 90.83 ± 1.37%. The antioxidant capacity of astaxanthin was not affected by the encapsulation, which demonstrated the effect of prolonging the release of active ingredients due to the protection of the biological activity of astaxanthin by encapsulation. Compared with the astaxanthin ethanol solution, the ASX-LNC had a slow-release effect and could prolong the action time of active substances. Overall, ASX-LNC is a potential carrier for application in food and health products, which can control the release of active substances. [ABSTRACT FROM AUTHOR]

The purpose of this study was to evaluate the astaxanthin-loaded nanostructured lipid carriers (ASX-NLC) prepared using a high-pressure homogenization transport system for local application of astaxanthin. Dynamic light scattering (DLS) and X-ray diffraction (XRD) were used to study the effect of microencapsulation on the properties of ASX-NLC. The mean size of ASX-NLC was about 108.43 ± 0.26 nm and PdI was 0.176 ± 0.002. The ASX-NLC had high encapsulation efficiency which was 95.69 ± 0.13%. Good light stability and temperature stability were shown at the ASX-NLC, indicating that the preparation process was feasible. The 2,2-diphenyl-1-pyridylohydrazinyl (DPPH) scavenging test showed that ASX-NLC could still play an antioxidant role. In vitro release studies showed that compared with an astaxanthin ethanol solution, an ASX-NLC could maintain astaxanthin release more effectively. In vitro permeation studies showed that ASX-NLC could increase astaxanthin retention in the skin. In conclusion, ASX-NLC could significantly enhance astaxanthin accumulation during dermal applications. The research results have important reference significance for local skin applications and provide a basis for the development of nanostructured lipid carriers. ASX-NLC might be suitable carriers for the local application of astaxanthin. Graphical Abstract [ABSTRACT FROM AUTHOR]